SABIC Innovative Plastics LNP THERMOCOMP JF006EXZ PES
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP JF006EXZ PES.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* JF006EXZ is a compound based on Polyethersulfone resin containing 30% Glass Fiber. Added features of this material include: Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.210 % | 0.210 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 139 MPa | 20200 psi | ASTM D638 |
| 145 MPa | 21000 psi | ISO 527 | |
| Elongation at Break | 1.9 % | 1.9 % | ISO 527 |
| 2.6 % | 2.6 % | ASTM D638 | |
| Flexural Strength | 192 MPa | 27800 psi | ASTM D790 |
| 209 MPa | 30300 psi | ISO 178 | |
| Flexural Modulus | 8.91 GPa | 1290 ksi | ASTM D790 |
| 9.70 GPa | 1410 ksi | ISO 178 | |
| Izod Impact, Notched | 0.770 J/cm | 1.44 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.50 J/cm | 10.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J | 4.43 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 1004 R Polypropylene
- ND Industries DriveGrip Anti Cam-Out Fluid
- Qualchem Danamid AFGF-20 Polyamide 66, 20% Glass Fiber
- Johnson Matthey Matti-sil 18Si Cadmium Free Brazing Alloy
- Momentive Performance Materials RTV5242 White Adhesive Sealant, Fast Cure Paste
- Solvay REPEL-O-TEX® PF-594 Surfactant
- Teknor Apex Telcar® TL-1522E Thermoplastic Elastomer
- Toho Tenax Besfight® G40-800 12K IMA5C EP03 Continuous Filament Carbon Fiber
- Eurotec® Tecomid® NA40 NL XA 20 PA 6.6 unreinforced, UL94 V0
- Ascend Performance Materials Vydyne® R533H NAT Nylon 66, 33% Glass Reinforced, Conditioned
Copyright © lookpolymers.com All Rights Reserved