SABIC Innovative Plastics LNP THERMOCOMP QF007 PA 6/10
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP QF007 PA 6/10.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* QF007 is a compound based on Nylon 6/10 resin containing 35% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.370 % | 0.370 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0040 cm/cm @Time 86400 sec |
0.0010 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 156 MPa | 22600 psi | Type I, 5 mm/min; ASTM D638 |
| 157 MPa | 22800 psi | 5 mm/min; ISO 527 | |
| 176 MPa | 25500 psi | ASTM D638 | |
| Tensile Strength, Yield | 156 MPa | 22600 psi | Type I, 5 mm/min; ASTM D638 |
| 157 MPa | 22800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D638 |
| 2.4 % | 2.4 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D638 |
| 2.4 % | 2.4 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 9.60 GPa | 1390 ksi | 1 mm/min; ISO 527 |
| 9.97 GPa | 1450 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 227 MPa | 32900 psi | ISO 178 |
| 238 MPa | 34500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 268 MPa | 38900 psi | ASTM D790 | |
| Flexural Yield Strength | 239 MPa | 34700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 7.93 GPa | 1150 ksi | 2 mm/min; ISO 178 |
| 8.32 GPa | 1210 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 8.90 GPa | 1290 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.24 J/cm | 2.32 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.8 J/cm | 20.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 65.0 kJ/m² | 30.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
19.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 114 µm/m-°C @Temperature -30.0 - 30.0 °C |
63.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 222 °C @Thickness 3.20 mm |
432 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 214 °C @Thickness 3.20 mm |
417 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- 3M Dyneon™ TF 4303 PTFE 15% Graphite Filled (discontinued **)
- SABIC Innovative Plastics ULTEM 1000EF PEI (Asia Pacific)
- Solvay RHODASURF® LA-23/6.5 Surfactant
- A. Schulman POLYTROPE™ TPP 524 Injection Molding Grade Olefinic Thermoplastic Elastomer
- 3M 5498 PTFE Film Tape
- American Computer Optics Medium-High Transmission Filter 3 mm
- Petroquimica Triunfo Trithene® SX 9003 MDPE - Blow Molding
Copyright © lookpolymers.com All Rights Reserved