SABIC Innovative Plastics LNP THERMOCOMP RF006EXZ PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF006EXZ PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* RF006EXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.870 % | 0.870 % | 50% RH, 24 hrs; ASTM D570 |
| 1.07 % | 1.07 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | ASTM D638 |
| 140 MPa | 20300 psi | ISO 527 | |
| Elongation at Break | 2.3 % | 2.3 % | ASTM D638 |
| 2.6 % | 2.6 % | ISO 527 | |
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
| 9.85 GPa | 1430 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| 217 MPa | 31500 psi | ISO 178 | |
| Flexural Modulus | 7.44 GPa | 1080 ksi | ASTM D790 |
| 8.90 GPa | 1290 ksi | ISO 178 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.31 J/cm | 13.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 46.0 kJ/m² | 21.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 26.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 29.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.5 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 74.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 74.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 222 °C | 432 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 230 °C @Thickness 3.20 mm |
446 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Poco Graphite SUPERSiC® Si Silicon Carbide
- Nilit FRIANYL A63 BR80 Nylon 6.6 for injection molding, 80% bronze filled
- Parker Chomerics SOFT-SHIELD® 4002 Low Closure Force, Foam Core EMI Gasket
- Abatron AboWeld 8101-9/AboCure 8101-9 Epoxy (discontinued **)
- Lehmann & Voss LUVOCOM® 50/CF/30 Polycarbonate, with carbon fiber
- LG Chemical LG-475 Styrene-Butadiene-Styrene
- Techmer ES Electrafil® J-50/CF/10/TF/15 Polycarbonate, 10% Carbon Fiber Reinforced, 15% PTFE
- DuPont Elvax® 3124 Ethylene-Vinyl Acetate Copolymer Resin for Extrusion Coating
- Hexcel® Redux® 335K Adhesive film for bonding metallic and composite components (0.06 psf)
- Akro-Plastic Akromid® A3 GM 10/20 S1 PA, 10% Glass Filled, 20% Mineral Filled, Cold-Impact Resistant (discont
Copyright © lookpolymers.com All Rights Reserved