SABIC Innovative Plastics LNP Thermocomp XF006S

Category Polymer , Thermoplastic , Nylon , Amorphous Nylon
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp XF006S.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* XF006S is a compound based on Amorphous Nylon containing Glass Fiber. Characteristics of this grade are: Heat Stabilized.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.36 g/cc
1.36 g/cc
ASTM D 792
Density 1.36 g/cc
0.0491 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.28 %
0.28 %
23°C / 50% RH; ISO 62
0.22 %

@Time 86400 sec
 0.22 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Transverse 0.0020 - 0.0040 cm/cm

@Time 86400 sec
 0.0020 - 0.0040 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 138 MPa
20000 psi
Type I, 5 mm/min; ASTM D 638
141 MPa
20500 psi
5 mm/min; ISO 527
Elongation at Break 2.5 %
2.5 %
5 mm/min; ISO 527
2.6 %
2.6 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 9.02 GPa
1310 ksi
1 mm/min; ISO 527
9.65 GPa
1400 ksi
50 mm/min; ASTM D 638
Flexural Strength 208 MPa
30200 psi
1.3 mm/min, 50 mm span; ASTM D 790
214 MPa
31000 psi
ISO 178
Flexural Yield Strength 209 MPa
30300 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 8.91 GPa
1290 ksi
2 mm/min; ISO 178
9.06 GPa
1310 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.560 J/cm

@Temperature 23.0 °C
 1.05 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 6.32 J/cm

@Temperature 23.0 °C
 11.8 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 38.0 kJ/m²

@Temperature 23.0 °C
 18.1 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
11.0 J

@Temperature 23.0 °C
 8.11 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 44.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 24.4 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
CTE, linear, Transverse to Flow 35.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 19.4 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 144 °C
291 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
142 °C

@Thickness 3.20 mm
 288 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 137 °C
279 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
138 °C

@Thickness 3.20 mm
 280 °F

@Thickness 0.126 in
 unannealed; ASTM D 648