Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 2.10 GPa | 305 ksi | |
Plastcom SLOVASTER® B1 BT TS PBT, basic type FeaturesPBT basic type for injection molding. Melt is characterised by outstanding fluidity, which enables injection molding of complicated and divided products also on multiple molds. Anisotropy of.. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycoloy® CY100FC PC+ABS High impact PC+ABS material designed for local Pacific Automotive applications |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Lexan® EXL1036 PC Copolymer Lexan* EXL1036 polycarbonate (PC) siloxane copolymer resin is a UV stabilized high viscosity grade designed for (co-)extrusion. This resin offers extreme low temperature (-60 C) ductility and good h.. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | ISO 178 |
SABIC Innovative Plastics LNP Colorcomp D10009 PC LNP* Colorcomp* D10009 is a compound based on Polycarbonate resin containing Flame Retardant, Unfilled Custom Color. Added features of this material include: Flame Retardant.This data was supplied .. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | ASTM D790 |
Solvay Specialty Polymers Amodel® AT-5001 Polyphthalamide (PPA) Resin, Dry as Molded
(discontinued **) AMODEL AT-5001 polyphthalamide resin is a neat ductile material that offers superior retention of properties after humid thermal aging, high impact at low temperature, and better mechanical properti.. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | 0.1 in/min; ASTM D790 |
Ineos Nova 8077 High Performance Styrenic Enhanced Polystyrene
(discontinued **) High flow, Special additives can be incorporate to improve properties such as coefficient of friction and static dissipation, Custom colorsApplications: Injection molding, Designed for thin wall app.. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | 1.5 mm/min; ISO 178:2001 |
Global EPP PA 6E Extruded Polyamide 6 Polyamides, commonly referred to as nylons, are macromolecular, partially crystalline thermoplastics. Their physical properties are mainly determined by the composition and structure of their molecu.. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | |
Lehmann & Voss LUVOCOM® AC-80/TF/22/BK Polyacetal-copolymer, with PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, gl.. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | ASTM D790 |
Ineos ABS TRIAX® 1120 ABS/Nylon Blend, Injection Grade, Dry as Molded Injection molding grade with good flow and stress corrosion cracking resistance, good chemical resistance (fuel, cleaning agents), high impact and notched impact strength, good acoustical damping be.. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | ISO 178 |
Grupo Repol Dinalon® C1S25 PA6/PA66 Blend, Unreinforced Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DL004 PC (Europe-Africa-Middle East) LNP* LUBRICOMP* DL004 is a compound based on Polycarbonate resin containing PTFE. Added features include Internally Lubricated. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP KL003E POM (Europe-Africa-Middle East) LNP* LUBRICOMP* KL003E is a compound based on Acetal Copolymer resin containing PTFE. Added features include: Internally Lubricated, Easy Molding. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP KL004L Acetal Copoly (Asia Pacific) LNP* Lubricomp* KL004L is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated, Low Extractible. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP KL004L Acetal Copolymer LNP* LUBRICOMP* KL004L is a compound based on Acetal Copolymer resin containing 20% PTFE. Added features of this material include: Wear Resistant, Low Extractible. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON CD000I PS LNP* Stat-kon* CD000I is a compound based on Polystyrene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL PX1005X PPE+HIPS (Europe-Africa-Middle East) Noryl PX1005X is an unfilled, low heat resistance, halogen free (according VDE/DIN 472 part 813) flame retardant material. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® K3501 PBT (Europe-Africa-Middle East) Unfilled PBT, Hydrollytically Stable, Heat Stabilized, Impact Modified. A hydrollytically stable grade designed for improved performance under heat/humidity environments. Targeted at automotive unde.. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | ASTM-D790 |
Polyram RamShine PV507 ABS, Flame Retardant Flame retardant ABS for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | ISO 178 |
Zeon Chemicals Zeonor® 1060R Cyclo Olefin Polymer Zeonor® is a line of thermoplastic polyolefin resin with an excellent combination of optical and electronic properties. These unique Cyclo Olefin Polymer (COP) was developed by Zeon Corporation usi.. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | ASTM D790 |
Unitika U-100 Engineering Plastic CAS No: 26590-50-1Information provided by Unitika Ltd. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | ASTM D790 |
Eastman Amphora™ AM1800 3D Polymer Eastman Amphora™ 3D polymer is a low-odor, styrene-free choice that was developed for 3D Printing applications. With Amphora, makers can create items that are more functional, durable, efficient, a.. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | ASTM D790 |
Covestro Makrolon® T 7435 Polycarbonate, High Impact Impact modified injection molding grade, extremely easy flow and easy mold release, housings for portable mobile phones.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience wa.. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | DIN 52457 |
CP-Polymer-Technik Wellamid® 6600/42 HWCP Nylon 66, Polymer Modified, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | ISO 178 |
BASF Ultramid® S3K Balance PA 610 (Dry) Description: BASF supplies polyamide 610 for processing by injection molding under the trade name Ultramid® Balance which is produced by polycondensation of hexamethylene diamine and sebacic acid. .. |
|||
Flexural Modulus | 2.10 GPa @Temperature 23.0 °C |
305 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PPHC T8020 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL RN0612 PPE+HIPS (Europe-Africa-Middle East) Noryl RN0612 is an unfilled Post Consumer recycle (PCR) based injection moldable modified polyphenylene ether resin comprising at least 30% PCR styrenic series resin content. Designed for good dimen.. |
|||
Flexural Modulus | 2.10 GPa | 305 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® V3900WX PBT+PC (Europe-Africa-Middle East) PBT/PC blend - Unreinforced - Flame Retardant. This is a UV-stabilized grade designed for outdoor enclosure applications requiring UL 746C F1 weatherability performance. |
|||
Flexural Modulus | 2.10 - 5.52 GPa | 305 - 800 ksi | Average value: 3.31 GPa Grade Count:25 |
Overview of materials for Polypropylene with 30% Mica Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Mica Filler". Specific grades with primary filler content between 25% and 34% are.. |