SABIC Innovative Plastics LNP LUBRICOMP DL004 PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DL004 PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* DL004 is a compound based on Polycarbonate resin containing PTFE. Added features include Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 5.3 % | 5.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 2.10 GPa | 305 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 77.0 MPa | 11200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | 80*10*4; ISO 180/1A |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.21 | 0.21 | ASTM D3702 Modified |
| K (wear) Factor | 62.4 x 10-8 mm³/N-M | 31.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 79.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
43.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 79.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
43.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-1 @Thickness 3.00 mm |
V-1 @Thickness 0.118 in |
UL 94 |
Users viewing this material also viewed the following:
- Pyrotek Pyroboard™ S1150 Roller
- SABIC Innovative Plastics Lexan® PC1800R PC (Asia Pacific)
- Solvay Specialty Polymers Veradel® A-100, A-200, A-300 Polyethersulfone (discontinued **)
- Fiberfil® PP-60/CC/40 Polypropylene Homopolymer, 40% Calcium Carbonate
- Spartech EP6220 Filled and Reinforced Copolymer
- Total Lumicene® mPE M5220 M Metallocene High Density Polyethylene
- Dow Corning XIAMETER® PMCPPMX-200 200CS Silicone Fluid
- CMW® D581F Silver Graphite Contact Material
- E-Polymers TEKAPPO® JF201 Filler Reinforced Heat Resistant Dimensional Stability Flame Retardant M-PPO
- 3M 7733FLW Overlaminating Film
Copyright © lookpolymers.com All Rights Reserved