SABIC Innovative Plastics Valox® K3501 PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® K3501 PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unfilled PBT, Hydrollytically Stable, Heat Stabilized, Impact Modified. A hydrollytically stable grade designed for improved performance under heat/humidity environments. Targeted at automotive underhood applications requiring USCAR-2 Class III humidity/heat performance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0800 % | 0.0800 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.34 % | 0.34 % | ISO 62 |
| Melt Index of Compound | 26 g/10 min @Load 2.16 kg, Temperature 250 °C |
26 g/10 min @Load 4.76 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 25.0 MPa | 3630 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D638 |
| 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 40 % | 40 % | 50 mm/min; ISO 527 |
| 50 % | 50 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 3.5 % | 3.5 % | Type I, 50 mm/min; ASTM D638 |
| 3.5 % | 3.5 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.10 GPa | 305 ksi | 1 mm/min; ISO 527 |
| 2.40 GPa | 348 ksi | 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 70.0 MPa | 10200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
| 2.10 GPa | 305 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| 0.750 J/cm @Temperature -20.0 °C |
1.41 ft-lb/in @Temperature -4.00 °F |
ASTM D256 | |
| 0.800 J/cm @Temperature 0.000 °C |
1.50 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 91.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
50.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 97.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
53.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 45.0 °C | 113 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 45.0 °C @Thickness 3.20 mm |
113 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 165 °C | 329 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- NYCOA 1417 HS Heat Stabilized, Impact Modified Nylon 6 Resin
- PolyOne Geon™ Vinyl Wire & Cable WJB593KBL Polyvinyl Chloride, Flexible (PVC, Flexible)
- PolyOne LubriOne™ 5209 FPL 20 Natural Acetal (POM) Copolymer
- Abatron AboCast 8-10/Abocure 8-10 Epoxy (discontinued **)
- Shuman FR910V0 Utility Black Polycarbonate Flame Retardant
- Samsung Cheil Industries Infino® HI-1001BN PC/ABS, Unreinforced
- A. Schulman POLYFLAM™ E-17338 22% CACO3 Filled Copolymer Polypropylene
- Total PS CPDS 820 Flame Retardant Polystyrene
- C.O.I.M. LARIPUR® LPR9025 Special Adipate Ester Polyurethane
- 3M HGS18000 Glass Bubbles
Copyright © lookpolymers.com All Rights Reserved