Polykemi AB POLYfill PPHC T8020 Polypropylene, Mineral Reinforced

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler
Manufacturer Polykemi AB
Trade Name POLYfill
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYfill PPHC T8020 Polypropylene, Mineral Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Filler Content 20 %
20 %
±2%; Polykemi
Linear Mold Shrinkage 0.010 - 0.012 cm/cm
0.010 - 0.012 in/in
Across Flow; ISO 2577
0.010 - 0.012 cm/cm
0.010 - 0.012 in/in
With Flow; ISO 2577
Melt Index of Compound 8.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 8.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 30.0 MPa
<= 4350 psi
ISO/R527
Elongation at Yield 7.0 %
7.0 %
ISO/R527
Flexural Strength <= 47.0 MPa
<= 6820 psi
ISO 178
Flexural Modulus 2.10 GPa

@Temperature 23.0 °C
 305 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 0.300 J/cm²

@Temperature -20.0 °C
 1.43 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
0.450 J/cm²

@Temperature 23.0 °C
 2.14 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 115 °C
239 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 63.0 °C
145 °F
120°C/h; ISO 75/1
Vicat Softening Point 83.0 °C

@Load 5.001 kg
 181 °F

@Load 11.03 lb
 50°C/h; ISO 306
144 °C

@Load 1.00 kg
 291 °F

@Load 2.21 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Glow Wire Test 750 °C

@Thickness 2.00 mm
 1380 °F

@Thickness 0.0787 in
 IEC 695-2-1