Polymer Property : Tensile Strength, Ultimate = 10.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	10.0 MPa	1450 psi
3M Dyneon™ Fluorel™ FE-5730Q Fluoroelastomer VF2 + HFP + TFE Terpolymer (discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 69.2%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. 69.2% F grade terpolymer with good pe..
Tensile Strength, Ultimate	10.0 MPa	1450 psi	500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Eastman 1924P Polyethylene (discontinued **) Low-density polyethylene 1924P is a resin in the boardstock coating industry for use in breadboard, cupstock, and liquid packaging board. This material has an excellent combination of low neck-in, ..
Tensile Strength, Ultimate	10.0 MPa	1450 psi	500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Eastman 808P Polyethylene (discontinued **) Low density polyethylene 808P is a low density resin designed for applications, such as sugar pouches and freezer wrap, where high coating speeds and good drawdown are required. The combination of ..
Tensile Strength, Ultimate	10.0 MPa	1450 psi	ASTM D638
Global MM-1018 Low Density Polyethylene, Lamination Coating Grade (discontinued **) Description-transparency, high toughness, flexibility, high impact strength, good chemical resistanceApplications-laminates, coating applications, food applicationsMeets FDA requirements as listed i..
Tensile Strength, Ultimate	10.0 MPa	1450 psi	ASTM D638
Global JJ-4324 Low Density Polyethylene, Film Extrusion Grade (discontinued **) Description-transparency, high toughness, flexibility, high impact strength, good chemical resistanceApplications-bagsMeets FDA requirements as listed in food additives regulation 21 CFR 117.1520 fo..
Tensile Strength, Ultimate	10.0 MPa	1450 psi	ASTM D638
Huntsman PE1058 Film Extrusion Polyethylene (discontinued **) Homopolymer and FDA compliant.Features: Exceptional draw down and processability, excellent strength, good heat sealability, and optics.Applications: Film extrusion: all thin film uses and especiall..
Tensile Strength, Ultimate	10.0 MPa	1450 psi	ASTM D638
Huntsman PE5032 Extrusion Coating Polyethylene (discontinued **) Homopolymer and FDA compliant.Features: Excellent draw down, low neck-in, excellent heat sealability, good adhesion, low smoking, no edge weave, and excellent printability.Applications: Extrusion: c..
Tensile Strength, Ultimate	10.0 MPa	1450 psi	ASTM D638
Huntsman PE5080 Extrusion Coating Polyethylene (discontinued **) Homopolymer and FDA compliant.Features: Excellent draw down, low neck-in, and excellent adhesion.Applications: Extrusion: coating grade and thin coatings.FDA Notes: Conforms to FDA regulation 21 CFR..
Tensile Strength, Ultimate	10.0 - 35.2 MPa	1450 - 5110 psi	Average value: 26.2 MPa Grade Count:22
Overview of materials for Polypropylene with 20% Mica Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Mica Filler". Specific grades with primary filler content between 15% and 24% are..
Tensile Strength, Ultimate	10.0 - 105 MPa @Temperature 60.0 - 150 °C	1450 - 15200 psi @Temperature 140 - 302 °F	Average value: 50.2 MPa Grade Count:6
Overview of materials for Nylon 6, Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass Fiber Filled, Flame Retardant". Each property range of values reported is minimum and max..
Tensile Strength, Ultimate	10.0 - 95.0 MPa @Strain 1.00 - 3.00 %	1450 - 13800 psi @Strain 1.00 - 3.00 %	Average value: 49.1 MPa Grade Count:1
Overview of materials for Nylon 66, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum ..
Tensile Strength, Ultimate	10.0 MPa	1450 psi
Sylvin Technologies 9915-60 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc.
Tensile Strength, Ultimate	10.0 MPa	1450 psi	GB/T 528
Chengdu Polyster 7500 General Grade TPV Information provided by Chengdu Polyster Co., Ltd.
Tensile Strength, Ultimate	10.0 MPa	1450 psi	ISO 527-1
Chengdu Polyster CH4132 Thermoplastic Polyether-ester Elastomer (TPEE) Poly-basic block copolymer. Good compatibility with POM. For blending with POM to improve impact resilience properties.Information provided by Chengdu Polyster Co., Ltd.
Tensile Strength, Ultimate	10.0 MPa	1450 psi
Dow Corning SILASTIC® 7-6860 BIOMEDICAL GRADE LSR, KIT Silastic® BioMedical Grade Liquid Silicone Rubbers are heat cured elastomer raw materials for use by customers fabricating medical devices.Information provided by Dow Corning
Tensile Strength, Ultimate	10.0 MPa	1450 psi
Dow Corning SILASTIC® Q7-4750 BIOMEDICAL GRADE ETR ELASTOMER, KIT Two-part, platinum-catalyzed (1:1 by weight), enhanced tear-resistant silicone elastomers are heat cured high consistency silicone rubbers designed for use by customers fabricating medical devices.I..
Tensile Strength, Ultimate	10.0 MPa	1450 psi
Dow DOWLEX™ IP-42 High Density Polyethylene DOWLEX® IP-42 resin is an improved processing high density polyethylene resin designed for excellent flow and high impact. DOWLEX IP-42 resin is designed by optimizing the breadth and shape of the ..
Tensile Strength, Ultimate	10.0 MPa	1450 psi
Dow DOWLEX™ IP-60 High Density Polyethylene DOWLEX® IP-60 resin is an improved processing high density polyethylene resin designed to offer excellent processability, good impact and top load strength required in thin wall injection molding. ..
Tensile Strength, Ultimate	10.0 MPa	1450 psi
Dow DOWLEX™ IP-90 High Density Polyethylene Next Generation DOWLEX® IP-90 resin is a high flow improved processing high density polyethylene resin designed for ultra-thin wall injection molded containers and drink cups. This resin has been m..
Tensile Strength, Ultimate	10.0 - 43.0 MPa	1450 - 6240 psi	Average value: 21.4 MPa Grade Count:141
Overview of materials for High Density Polyethylene (HDPE), Injection Molded This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Injection Molded". Each property range of values reported is minimum a..
Tensile Strength, Ultimate	10.0 - 30.0 MPa	1450 - 4350 psi	Average value: 22.5 MPa Grade Count:11
Overview of materials for Polymethylpentene, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polymethylpentene, Molded". Each property range of values reported is minimum and maximum values of appr..
Tensile Strength, Ultimate	10.0 - 135 MPa @Temperature 60.0 - 150 °C	1450 - 19600 psi @Temperature 140 - 302 °F	Average value: 68.8 MPa Grade Count:4
Overview of materials for Polyethersulfone (PES) This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone". Each property range of values reported is minimum and maximum values of appropriate M..
Tensile Strength, Ultimate	10.0 - 135 MPa @Temperature 60.0 - 150 °C	1450 - 19600 psi @Temperature 140 - 302 °F	Average value: 70.2 MPa Grade Count:2
Overview of materials for Polyethersulfone (PES), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% ..
Tensile Strength, Ultimate	10.0 MPa	1450 psi	ASTM D638
Huntsman Rexell® H2104 Injection Molding LLDPE (discontinued **) Linear-low high density homopolymer, injection molding, FDA compliant.Features: High flow and short cycle times.Applications: Thin wall containers.FDA Notes: Conforms to FDA regulation 21 CFR 177.15..
Tensile Strength, Ultimate	10.0 - 100 MPa @Temperature -20.0 - 100 °C	1450 - 14500 psi @Temperature -4.00 - 212 °F	Average value: 45.0 MPa Grade Count:2
Overview of materials for Nylon 6, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Unreinforced". Each property range of values reported is minimum and maximum values of appropri..
Tensile Strength, Ultimate	10.0 - 100 MPa @Strain 1.00 - 8.00 %	1450 - 14500 psi @Strain 1.00 - 8.00 %	Average value: 45.0 MPa Grade Count:2
Overview of materials for Nylon 6, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Unreinforced". Each property range of values reported is minimum and maximum values of appropri..
Tensile Strength, Ultimate	10.0 - 65.0 MPa	1450 - 9430 psi	Average value: 23.8 MPa Grade Count:133
Overview of materials for Polypropylene, Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Mineral Reinforced". Each property range of values reported is minimum and maximum values..