- Polymer Property : Tensile Strength, Ultimate = 1450 psi
Polymer Property : Tensile Strength, Ultimate = 1450 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | |
| 3M Dyneon™ Fluorel™ FE-5730Q Fluoroelastomer VF2 + HFP + TFE Terpolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 69.2%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. 69.2% F grade terpolymer with good pe.. |
|||
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
| Eastman 808A Polyethylene
(discontinued **) Low density polyethylene 808A is a general-purpose formulation used for injection molding and general-purpose extrusion.Unless otherwise noted, all tests are run at 23°C and 50% RH.Information from.. |
|||
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
| Eastman 808P Polyethylene
(discontinued **) Low density polyethylene 808P is a low density resin designed for applications, such as sugar pouches and freezer wrap, where high coating speeds and good drawdown are required. The combination of .. |
|||
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Global MM-1018 Low Density Polyethylene, Lamination Coating Grade
(discontinued **) Description-transparency, high toughness, flexibility, high impact strength, good chemical resistanceApplications-laminates, coating applications, food applicationsMeets FDA requirements as listed i.. |
|||
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Huntsman PE1044 Film Extrusion Polyethylene
(discontinued **) Homopolymer, and FDA compliant.Features: Yields film with excellent optical and machinability.Applications: Film extrusion: soft goods and other high clarity packaging.FDA Notes: Conforms to FDA reg.. |
|||
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Huntsman PE1068 Film Extrusion Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Exceptional draw down and processability even to 1/2 mil; excellent strength, good heat sealability, and good optical.FDA Notes: Conforms to FDA regulation 21.. |
|||
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Huntsman PE5080 Extrusion Coating Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Excellent draw down, low neck-in, and excellent adhesion.Applications: Extrusion: coating grade and thin coatings.FDA Notes: Conforms to FDA regulation 21 CFR.. |
|||
| Tensile Strength, Ultimate | 10.0 - 19.0 MPa | 1450 - 2760 psi | Average value: 13.7 MPa Grade Count:8 |
| Overview of materials for High Density Polyethylene (HDPE), Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Impact Grade". Each property range of values reported is minimum and m.. |
|||
| Tensile Strength, Ultimate | 10.0 - 105 MPa @Temperature 60.0 - 150 °C |
1450 - 15200 psi @Temperature 140 - 302 °F |
Average value: 50.2 MPa Grade Count:6 |
| Overview of materials for Nylon 6, Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass Fiber Filled, Flame Retardant". Each property range of values reported is minimum and max.. |
|||
| Tensile Strength, Ultimate | 10.0 - 95.0 MPa @Temperature -20.0 - 100 °C |
1450 - 13800 psi @Temperature -4.00 - 212 °F |
Average value: 49.1 MPa Grade Count:1 |
| Overview of materials for Nylon 66, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum .. |
|||
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Multibase Multi-Flex® A 9402 AH Black TPE Thermoplastic Elastomer Forms: PelletsProcessing Methods:Injection Molding Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D412 |
| Multibase Multi-Flex® TPE A 5703 BLK The burn rate is 1.2 in/min (30 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ISO 527-1 |
| Chengdu Polyster CH4132 Thermoplastic Polyether-ester Elastomer (TPEE) Poly-basic block copolymer. Good compatibility with POM. For blending with POM to improve impact resilience properties.Information provided by Chengdu Polyster Co., Ltd. |
|||
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Huntsman PE2040 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Good molding processability, produces parts that are flexible, and show excellent flatness in large projected areas.Applications: Injection molding: general p.. |
|||
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Huntsman PE2065 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: General purpose injection molding resin with good flow characteristicsApplications: Injection molding: lids.FDA Notes: Conforms to FDA regulation 21 CFR 177.1.. |
|||
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Huntsman PE2067 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: High flow resin, provides excellent gloss and surface characteristics, and minimum cycle time.Applications: Injection molding: lids.FDA Notes: Conforms to FDA.. |
|||
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638-95 |
| Multibase Multi-Flex® TPO D 5308 BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302.Data provided by Multibase. |
|||
| Tensile Strength, Ultimate | 10.0 - 43.0 MPa | 1450 - 6240 psi | Average value: 21.4 MPa Grade Count:141 |
| Overview of materials for High Density Polyethylene (HDPE), Injection Molded This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Injection Molded". Each property range of values reported is minimum a.. |
|||
| Tensile Strength, Ultimate | 10.0 - 30.0 MPa | 1450 - 4350 psi | Average value: 22.5 MPa Grade Count:11 |
| Overview of materials for Polymethylpentene, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polymethylpentene, Molded". Each property range of values reported is minimum and maximum values of appr.. |
|||
| Tensile Strength, Ultimate | 10.0 - 135 MPa @Temperature 60.0 - 150 °C |
1450 - 19600 psi @Temperature 140 - 302 °F |
Average value: 68.8 MPa Grade Count:4 |
| Overview of materials for Polyethersulfone (PES) This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
| Tensile Strength, Ultimate | 10.0 - 135 MPa @Temperature 60.0 - 150 °C |
1450 - 19600 psi @Temperature 140 - 302 °F |
Average value: 70.2 MPa Grade Count:2 |
| Overview of materials for Polyethersulfone (PES), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% .. |
|||
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Huntsman Rexell® H2104 Injection Molding LLDPE
(discontinued **) Linear-low high density homopolymer, injection molding, FDA compliant.Features: High flow and short cycle times.Applications: Thin wall containers.FDA Notes: Conforms to FDA regulation 21 CFR 177.15.. |
|||
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | Molded property |
| Dow LDPE 535I Low Density Polyethylene, Liner Grade DOW LDPE 535I resin is a barefoot general purpose liner resin with medium clarity for medium modulus packaging applications. This material complies with U.S.FDA regulation 21 CFR 177.1520(c) 2.1 for.. |
|||
| Tensile Strength, Ultimate | 10.0 - 100 MPa @Temperature -20.0 - 100 °C |
1450 - 14500 psi @Temperature -4.00 - 212 °F |
Average value: 45.0 MPa Grade Count:2 |
| Overview of materials for Nylon 6, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Unreinforced". Each property range of values reported is minimum and maximum values of appropri.. |
|||
| Tensile Strength, Ultimate | 10.0 - 100 MPa @Strain 1.00 - 8.00 % |
1450 - 14500 psi @Strain 1.00 - 8.00 % |
Average value: 45.0 MPa Grade Count:2 |
| Overview of materials for Nylon 6, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Unreinforced". Each property range of values reported is minimum and maximum values of appropri.. |
|||
| Tensile Strength, Ultimate | 10.0 - 65.0 MPa | 1450 - 9430 psi | Average value: 23.8 MPa Grade Count:133 |
| Overview of materials for Polypropylene, Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Mineral Reinforced". Each property range of values reported is minimum and maximum values.. |
|||