Polymer Property : Flexural Yield Strength = 21800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	150 MPa	21800 psi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers Nima™ HL 30525 GF FR PET, 25% Glass Fiber PET – Flame Retardant 25% Short Glass Fiber Reinforced. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared according to ASTM s..
Flexural Yield Strength	150 MPa	21800 psi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers Opnyl OP6GF15 Nylon 6, 15% Glass Reinforced, Dry Nylon 6 - Glass reinforced (15 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. For Nylon compounds the m..
Flexural Yield Strength	150 MPa	21800 psi	1.3 mm/min; ASTM D790
Ovation Polymers RIGITRON 30525 GF FR PET, 25% Glass Reinforced PET – 25% Short Glass Fiber Reinforced with Flame retardant. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared according to AS..
Flexural Yield Strength	150 MPa @Temperature 90.0 °C	21800 psi @Temperature 194 °F	ISO 178, ASTM D790
Nilit Nilamid A G7 FR PH1 35% Glass Fiber Reinforced, Flame Retardant PA66 (with Red Phosphorous) Description: Nilamid A G7 FR PH1 combines flame retardancy with outstanding mechanical performance. This product has a UL 94 V0 listing 1.5 and a complete yellow card. The formulation has been optim..
Flexural Yield Strength	150 MPa	21800 psi	ISO 178, ASTM D790
Nilit Nilamid A3 H G3 ZB 13% Glass Reinforced High Impact PA66 Description: Nilamid A3 H G3 ZB (13% Glass Reinforced) was developed for applications that require a combination of high stiffness and good elongation or impact resistance. It is widely used for app..
Flexural Yield Strength	150 MPa	21800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics EXTEM XH1005 TPI Resin Thermoplastic Polyimide Extem* XH1005 Resin.
Flexural Yield Strength	150 MPa	21800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics EXTEM XH1005 TPI Resin (Europe-Africa-Middle East) Thermoplastic Polyimide Extem* XH1005 Resin.
Flexural Yield Strength	150 MPa	21800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics EXTEM XH1005F TPI Resin (Europe-Africa-Middle East) High Heat Amorphous TPI Blend, Tg 267C, High Continuous Use Temperature (CUT). EFSA Food Contact Approved. Material is UL listed. This material is RoHS compliant and also halogen free according VDE/..
Flexural Yield Strength	150 MPa	21800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® BFL2015 PC Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only
Flexural Yield Strength	150 MPa	21800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® BFL2015 PC (Asia Pacific) Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only
Flexural Yield Strength	150 MPa	21800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® BFL2015 PC (Europe-Africa-Middle East) Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only
Flexural Yield Strength	150 MPa	21800 psi	ASTM Data
BASF Capron® HPN 9333G Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned) (discontinued **) Capron HPN 9333G is a 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface a..
Flexural Yield Strength	150 - 188 MPa	21800 - 27300 psi	Average value: 171 MPa Grade Count:15
Overview of materials for Polycyclohexylenedimethylene Terephthalate (PCT), 30% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PCT or PCTA, 30% Glass Reinforced".Specific grades with glass content between 25% and 34% are included. ..
Flexural Yield Strength	150 MPa @Thickness 3.20 mm	21800 psi @Thickness 0.126 in	1.3mm/min; ASTM D790
LG Chemical LupoxÂ® NH2306F PBT+GF30% Description: Injection Molding, PBT+GF30%, Halogen Free Flame RetardantApplication: IT/OA, E&E (Connector)CAS No. 65997-17-3 and 24968-12-5Information provided by LG Chemical
Flexural Yield Strength	150 MPa	21800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DX07035 PC (Europe-Africa-Middle East) LNP* LUBRICOMP* DX07035 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Flame Retardant. Added features include: Flame retardant, Easy Molding, Internally Lubricated, Mold R..
Flexural Yield Strength	150 MPa	21800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL SE1GFN2 PPE+PS (Asia Pacific) PPE+PS blend. 20% Glass reinforced. Non-brominated, non-chlorinated FR system. UL94 V1 listing. Dielectric strength. Dimensional stability. Suitable for E/E applications.
Flexural Yield Strength	150 MPa	21800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP WFL33 PBT LNP* LUBRICOMP* WFL33 is a compound based on PBT containing 15% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant.
Flexural Yield Strength	150 MPa	21800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® 815 PBT (Europe-Africa-Middle East) VALOX 815 is a 15% glass reinforced PBT+PET blend with excellent surface finish. Applications: hot air gun housings assemblies, industrial glue guns, appliance housings and handles.
Flexural Yield Strength	150 MPa	21800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® 855 PBT (Europe-Africa-Middle East) VALOX 855 is 15% glass reinforced PBT+PET blend with improved surface appearance. Applications: external housings, steam irons, appliance housings and lighting parts.
Flexural Yield Strength	150 MPa	21800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® K4530 PBT (Europe-Africa-Middle East) 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors.
Flexural Yield Strength	150 MPa	21800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® VX5022 PBT (Europe-Africa-Middle East) VALOX VX5022 is a 20% glass fibre reinforced PBT+PC blend with low warpage characteristics. This grade is 5021 with reduced warpage.
Flexural Yield Strength	150 MPa	21800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics XenoyÂ® 6370 PBT+PC 30% glass-reinforced, impact modified thermoplastic alloy. Improved toughness and ductility.
Flexural Yield Strength	150 MPa	21800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL GFN2 PPE+HIPS (Asia Pacific) PPE+PS blend. 20% Glass reinforced. FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including pump..
Flexural Yield Strength	150 MPa	21800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL NH7114 PPE+HIPS (Asia Pacific) Noryl* NH7114 resin is a 20% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve UL94 flame ratings while offering an exceptional balance of streng..
Flexural Yield Strength	150 MPa	21800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL NH7114 PPE+HIPS (Europe-Africa-Middle East) Noryl* NH7114 resin is a 20% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve UL94 flame ratings while offering an exceptional balance of streng..
Flexural Yield Strength	150 MPa	21800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL PX138H PPE+HIPS (Asia Pacific) Modified PPO Resin with 20% Glass Fibre Reinforced
Flexural Yield Strength	150 MPa	21800 psi	ASTM D790
PlastxWorld Veroplas PB3150 Nylon 66 15% glass filled injection molding gradeInformation provided by PlastxWorld Inc.
Flexural Yield Strength	150 - 230 MPa	21800 - 33400 psi	ASTM D790
Chang Chun Plastic PBT4830 Fire Retardant & 30% Glass Fiber Enforced Grade PBT Information provided by Dowell Trading Company Ltd.
Flexural Yield Strength	150 - 230 MPa	21800 - 33400 psi	ASTM D790
Chang Chun Plastic PBT4130 Fire Retardant & 30% Glass Fiber Enforced Grade PBT Information provided by Dowell Trading Company Ltd.
Flexural Yield Strength	150 MPa	21800 psi	ASTM Data
BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned) (discontinued **) Capron HPN 9333G HS is a heat stabilized, 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with..