SABIC Innovative Plastics Valox® 815 PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 815 PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
VALOX 815 is a 15% glass reinforced PBT+PET blend with excellent surface finish. Applications: hot air gun housings assemblies, industrial glue guns, appliance housings and handles.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.26 % | 0.26 % | ISO 62 |
| Viscosity | 155000 cP | 155000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | on Tensile Bar; SABIC Method |
| 0.0040 - 0.0060 cm/cm @Thickness 1.50 - 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.0591 - 0.126 in |
SABIC Method | |
| 0.0060 - 0.0090 cm/cm @Thickness 3.20 - 4.60 mm |
0.0060 - 0.0090 in/in @Thickness 0.126 - 0.181 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.010 cm/cm | 0.0060 - 0.010 in/in | on Tensile Bar; SABIC Method |
| 0.0050 - 0.0080 cm/cm @Thickness 1.50 - 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.0591 - 0.126 in |
SABIC Method | |
| 0.0080 - 0.011 cm/cm @Thickness 3.20 - 4.60 mm |
0.0080 - 0.011 in/in @Thickness 0.126 - 0.181 in |
SABIC Method | |
| Melt Flow | 20 g/10 min @Load 5.00 kg, Temperature 250 °C |
20 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| 60 g/10 min @Load 5.00 kg, Temperature 265 °C |
60 g/10 min @Load 11.0 lb, Temperature 509 °F |
ASTM D1238 | |
| Melt Index of Compound | 12 g/10 min @Load 1.20 kg, Temperature 265 °C |
12 g/10 min @Load 2.65 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 50 g/10 min @Load 5.00 kg, Temperature 265 °C |
50 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| 120 | 120 | ISO 2039-2 | |
| Hardness, H358/30 | 102 MPa | 14800 psi | ISO 2039-1 |
| Tensile Strength at Break | 100 MPa | 14500 psi | Type I, 5 mm/min; ASTM D638 |
| 100 MPa | 14500 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 100 MPa | 14500 psi | Type I, 5 mm/min; ASTM D638 |
| 100 MPa | 14500 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 50 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| 4.0 % | 4.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 50 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 6.20 GPa | 899 ksi | 5 mm/min; ASTM D638 |
| 6.20 GPa | 899 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 145 MPa | 21000 psi | 2 mm/min; ISO 178 |
| 155 MPa | 22500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 150 MPa | 21800 psi | 2 mm/min; ISO 178 |
| 155 MPa | 22500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 5.00 GPa | 725 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 5.20 GPa | 754 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 |
| 0.600 J/cm @Temperature 0.000 °C |
1.12 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| 0.600 J/cm @Temperature -30.0 °C |
1.12 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 3.90 J/cm | 7.31 ft-lb/in | ASTM D4812 |
| 3.90 J/cm @Temperature -30.0 °C |
7.31 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature 0.000 °C |
2.86 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| 25.0 kJ/m² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/2C | |
| 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179/2C | |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| 0.700 J/cm² @Temperature -20.0 °C |
3.33 ft-lb/in² @Temperature -4.00 °F |
ISO 179/2C | |
| Taber Abrasion, mg/1000 Cycles | 17 | 17 | CS-17, 1 kg; SABIC Method |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| 5.60e+16 ohm-cm | 5.60e+16 ohm-cm | ASTM D257 | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.0 @Frequency 50.0 - 60.0 Hz |
3.0 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| 3.6 @Frequency 100 Hz |
3.6 @Frequency 100 Hz |
IEC 60250 | |
| 3.6 @Frequency 100 Hz |
3.6 @Frequency 100 Hz |
ASTM D150 | |
| Dielectric Strength | 16.0 kV/mm @Thickness 3.20 mm |
406 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 18.0 kV/mm @Thickness 1.00 mm |
457 kV/in @Thickness 0.0394 in |
short time; IEC 60243-1 | |
| 22.0 kV/mm @Thickness 3.20 mm |
559 kV/in @Thickness 0.126 in |
in air; ASTM D149 | |
| 23.6 kV/mm @Thickness 1.60 mm |
599 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 | |
| 24.0 kV/mm @Thickness 1.60 mm |
610 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 30.0 kV/mm @Thickness 0.800 mm |
762 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 3101-22 Fiberglass Reinforced Thermoset BMC
- H.C. Starck Grade HD 20 Boron Carbide, B4C
- Karina E 601D22/15 Crepe PVC Compound
- Lubrizol ESTANE® T5275 Ether Based Thermoplastic Polyurethane (European Grade)
- EMS-Grivory Grivory® FG 40 NL nat 6021 PA6
- Clariant Renol 6601FR Nylon 66, Flame Retardant
- Buckeye Polymers BP RPP 0511C Polypropylene, 5% Mineral Filled
- DuPont Performance Polymers Sorona® 2045G BK346A Polytrimethylene Terephthalate (PTT) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved