SABIC Innovative Plastics EXTEM XH1005 TPI Resin
| Category | Polymer , Thermoplastic , Polyimide, Thermoplastic |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Extem |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics EXTEM XH1005 TPI Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Thermoplastic Polyimide Extem* XH1005 Resin.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Water Absorption | 0.60 % @Time 173000 sec |
0.60 % @Time 48.0 hour |
ASTM D570 |
| Water Absorption at Saturation | 2.3 % | 2.3 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.012 cm/cm @Thickness 3.20 mm |
0.010 - 0.012 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.0 g/10 min @Load 6.60 kg, Temperature 367 °C |
6.0 g/10 min @Load 14.6 lb, Temperature 693 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 5 mm/min; ISO 527 |
| 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 101 MPa | 14600 psi | 5 mm/min; ISO 527 |
| 103 MPa | 14900 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 6.0 % | 6.0 % | 5 mm/min; ISO 527 |
| 15 % | 15 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 6.0 % | 6.0 % | 5 mm/min; ISO 527 |
| 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 3.16 GPa | 458 ksi | 1 mm/min; ISO 527 |
| 3.42 GPa | 496 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 150 MPa | 21800 psi | 2 mm/min; ISO 178 |
| 168 MPa | 24400 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.85 GPa | 413 ksi | 2 mm/min; ISO 178 |
| 3.13 GPa | 454 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.430 J/cm | 0.806 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Charpy Impact, Notched | 2.10 J/cm² | 9.99 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 20.0 J @Temperature 23.0 °C |
14.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 23.0 - 150 °C |
27.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 51.0 µm/m-°C @Temperature 23.0 - 150 °C |
28.3 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C @Thickness 3.20 mm |
482 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 235 °C @Thickness 3.20 mm |
455 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 237 °C @Thickness 6.40 mm |
459 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 252 °C | 486 °F | Rate B/50; ISO 306 |
| 252 °C | 486 °F | Rate B/120; ISO 306 | |
| 260 °C | 500 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- Chi Mei Wonderloy® PC-175D PC/ABS Alloy (discontinued **)
- Indium Corp. Indalloy® 181 Sn-Pb-Cd Solder Alloy
- Industrial Laminates/Norplex NP320E Cotton Fabric
- Mitsui APELâ„¢ APL5014DP Cyclo Olefin Copolymer (COC)
- Johnson Matthey Plumbsol Soft Solder/Flux
- Lucite International Lucite® 41 Acrylic Resin for Casting and Embedments
- Shakespeare WP-104 diameter 0.4 mm Weft Polyester Monofilament
- Teknor Apex Chemlon® 240 MH Nylon 6, 40% Short Glass Fiber Reinforced
- Aclo Accutech Polypropylene Homopolymer HP0334G20M10CL Glass/Mineral Reinforced Coupled
- A. Schulman POLYBATCH™ White LL8425 MG Concentrate Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved