SABIC Innovative Plastics Valox® 855 PBT (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® 855 PBT (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
VALOX 855 is 15% glass reinforced PBT+PET blend with improved surface appearance. Applications: external housings, steam irons, appliance housings and lighting parts.
Physical Properties Metric English Comments
Specific Gravity 1.50 g/cc
1.50 g/cc
ASTM D792
Density 1.50 g/cc
0.0542 lb/in³
ISO 1183
Filler Content 15 %
15 %
ASTM D229
Moisture Absorption 0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.45 %
0.45 %
ISO 62
Viscosity 135000 cP
135000 cP
Melt Viscosity, 260°C, 1500 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
on Tensile Bar; SABIC Method
0.0060 cm/cm

@Thickness 3.20 mm
0.0060 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0060 - 0.010 cm/cm
0.0060 - 0.010 in/in
on Tensile Bar; SABIC Method
Melt Flow 79 g/10 min

@Load 5.00 kg,
Temperature 266 °C
79 g/10 min

@Load 11.0 lb,
Temperature 511 °F
ASTM D1238
Melt Index of Compound 11 g/10 min

@Load 1.20 kg,
Temperature 265 °C
11 g/10 min

@Load 2.65 lb,
Temperature 509 °F
MVR [cm^3/10 min]; ISO 1133
32 g/10 min

@Load 5.00 kg,
Temperature 250 °C
32 g/10 min

@Load 11.0 lb,
Temperature 482 °F
MVR [cm^3/10 min]; ISO 1133
60 g/10 min

@Load 5.00 kg,
Temperature 265 °C
60 g/10 min

@Load 11.0 lb,
Temperature 509 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ISO 2039-2
Hardness, H358/30 126 MPa
18300 psi
ISO 2039-1
Tensile Strength at Break 100 MPa
14500 psi
Type I, 5 mm/min; ASTM D638
100 MPa
14500 psi
5 mm/min; ISO 527
Tensile Strength, Yield 100 MPa
14500 psi
Type I, 5 mm/min; ASTM D638
100 MPa
14500 psi
5 mm/min; ISO 527
Elongation at Break 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
3.0 %
3.0 %
5 mm/min; ISO 527
3.0 %
3.0 %
Flexural Strain, break, 2 mm/min; ISO 178
Elongation at Yield 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 6.50 GPa
943 ksi
5 mm/min; ASTM D638
6.50 GPa
943 ksi
1 mm/min; ISO 527
Flexural Strength 148 MPa
21500 psi
1.3 mm/min, 50 mm span; ASTM D790
150 MPa
21800 psi
2 mm/min; ISO 178
Flexural Yield Strength 148 MPa
21500 psi
1.3 mm/min, 50 mm span; ASTM D790
150 MPa
21800 psi
2 mm/min; ISO 178
Flexural Modulus 5.20 GPa
754 ksi
1.3 mm/min, 50 mm span; ASTM D790
5.40 GPa
783 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.550 J/cm
1.03 ft-lb/in
ASTM D256
0.550 J/cm

@Temperature 0.000 °C
1.03 ft-lb/in

@Temperature 32.0 °F
ASTM D256
0.550 J/cm

@Temperature -30.0 °C
1.03 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched 4.00 J/cm
7.49 ft-lb/in
ASTM D4812
4.00 J/cm

@Temperature -30.0 °C
7.49 ft-lb/in

@Temperature -22.0 °F
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature 0.000 °C
2.86 ft-lb/in²

@Temperature 32.0 °F
80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 25.0 kJ/m²
11.9 ft-lb/in²
80*10*4; ISO 180/1U
23.0 kJ/m²

@Temperature -30.0 °C
10.9 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact Unnotched 2.00 J/cm²
9.52 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eU
2.50 J/cm²
11.9 ft-lb/in²
ISO 179/2C
1.50 J/cm²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
2.50 J/cm²

@Temperature -30.0 °C
11.9 ft-lb/in²

@Temperature -22.0 °F
ISO 179/2C
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
ISO 179/2C
0.800 J/cm²
3.81 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.400 J/cm²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179/2C
Dart Drop, Total Energy 6.00 J

@Temperature 23.0 °C
4.43 ft-lb

@Temperature 73.4 °F
ASTM D3763
Taber Abrasion, mg/1000 Cycles 17
17
CS-17, 1 kg; SABIC Method
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 3.3

@Frequency 1.00e+6 Hz
3.3

@Frequency 1.00e+6 Hz
ASTM D150
3.3

@Frequency 1.00e+6 Hz
3.3

@Frequency 1.00e+6 Hz
IEC 60250
3.3

@Frequency 50.0 - 60.0 Hz
3.3

@Frequency 50.0 - 60.0 Hz
IEC 60250
3.5

@Frequency 100 Hz
3.5

@Frequency 100 Hz
ASTM D150
3.5

@Frequency 100 Hz
3.5

@Frequency 100 Hz
IEC 60250
Dielectric Strength 18.0 kV/mm

@Thickness 3.20 mm
457 kV/in

@Thickness 0.126 in
in oil; ASTM D149
18.0 kV/mm

@Thickness 3.20 mm
457 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
21.0 kV/mm

@Thickness 1.00 mm
533 kV/in

@Thickness 0.0394 in
short time; IEC 60243-1
25.0 kV/mm

@Thickness 1.60 mm
635 kV/in

@Thickness 0.0630 in
in oil; IEC 60243-1
25.0 kV/mm

@Thickness 1.60 mm
635 kV/in

@Thickness 0.0630 in
in oil; ASTM D149
33.0 kV/mm

@Thickness 0.800 mm
838 kV/in

@Thickness 0.0315 in
in oil; ASTM D149
33.0 kV/mm

@Thickness 0.800 mm
838 kV/in

@Thickness 0.0315 in
in oil; IEC 60243-1
Dissipation Factor 0.0010

@Frequency 100 Hz
0.0010

@Frequency 100 Hz
ASTM D150
0.0010

@Frequency 50.0 - 60.0 Hz
0.0010

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.0015

@Frequency 100 Hz
0.0015

@Frequency 100 Hz
IEC 60250
0.010

@Frequency 1.00e+6 Hz
0.010

@Frequency 1.00e+6 Hz
IEC 60250
0.015

@Frequency 1.00e+6 Hz
0.015

@Frequency 1.00e+6 Hz
ASTM D150