SABIC Innovative Plastics NORYL SE1GFN2 PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL SE1GFN2 PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS blend. 20% Glass reinforced. Non-brominated, non-chlorinated FR system. UL94 V1 listing. Dielectric strength. Dimensional stability. Suitable for E/E applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Water Absorption | 0.11 % @Time 86400 sec |
0.11 % @Time 24.0 hour |
ISO 62-1 |
| Moisture Absorption | 0.0400 % | 0.0400 % | 50% RH, 24 hrs; ISO 62-4 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 3.5 g/10 min @Load 5.00 kg, Temperature 280 °C |
3.5 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 3.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
3.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | 50 mm/min; ISO 527 |
| 120 MPa | 17400 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 2.5 % | 2.5 % | 50 mm/min; ISO 527 |
| 3.0 % | 3.0 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 6.40 GPa | 928 ksi | 1 mm/min; ISO 527 |
| 7.10 GPa | 1030 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 140 MPa | 20300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 150 MPa | 21800 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 5.50 GPa | 798 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 5.60 GPa | 812 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| 0.900 J/cm @Temperature -30.0 °C |
1.69 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 5.20 J/cm | 9.74 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| 27.0 kJ/m² @Temperature -30.0 °C |
12.8 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179/2C |
| Dart Drop, Total Energy | 18.0 J @Temperature 23.0 °C |
13.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 30.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 75.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 134 °C @Thickness 3.20 mm |
273 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 142 °C | 288 °F | Rate B/50; ASTM D1525 |
| 142 °C | 288 °F | Rate B/50; ISO 306 | |
| 144 °C | 291 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.04e+16 ohm-cm | 2.04e+16 ohm-cm | ASTM D257 |
| 2.04e+16 ohm-cm | 2.04e+16 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.34e+17 ohm | 1.34e+17 ohm | ASTM D257 |
| 1.34e+17 ohm | 1.34e+17 ohm | ROA; IEC 60093 | |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.93 @Frequency 1.00e+6 Hz |
2.93 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Dielectric Strength | 26.2 kV/mm @Thickness 1.60 mm |
665 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 |
| 26.2 kV/mm @Thickness 1.50 mm |
665 kV/in @Thickness 0.0591 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0034 @Frequency 1.00e+6 Hz |
0.0034 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 0.0034 @Frequency 1.00e+6 Hz |
0.0034 @Frequency 1.00e+6 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 2502 C Natural Polypropylene
- SABIC Innovative Plastics EXTEM XH1015F TPI Resin (Europe-Africa-Middle East)
- Polymer Resources PC-GP2-TFE5 Polycarbonate, 5% PTFE, Wear Resistant, Medium Flow
- ExxonMobil Escorene® LL-3113 LLDPE/Hexene Premium High Strength 1.2 mil Film (discontinued **)
- UBE UBESTA® 3030U Nylon 12 (After Ethylene Glycol for 1000 hours)
- CP-Polymer-Technik Wellamid® 6600 PA-66-HWV0CP UL-Licensed Nylon 66, Flame Protection, Heat Stabilized, Conditioned
- Chi Mei Kibisan® PN137H SAN Resin, General Purpose
- DuPont Performance Polymers Zytel® PLS 95G40DH1T BK261 Nylon 6 (Unverified Data**)
- ConocoPhillips Hydroclear® ATF Type F Automatic Transmission Fluid
- 3M Scotch-Weld™ CA100 Instant Adhesive
Copyright © lookpolymers.com All Rights Reserved