Arkema Group Rilsan® AZM 30 NOIR T6LD Nylon 12, 30% Glass Fiber Filled (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, 30% Glass Fiber Filled
Manufacturer	Arkema
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Rilsan® AZM 30 NOIR T6LD Nylon 12, 30% Glass Fiber Filled (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Designation ISO 1874-PA12,MHLR,16-060,GF30Rigid grade with glass fiber (30%) for injection molding. Available color: black. Reinforced light and heat stabilizing agent. Mold-release agent.High rigidity. High compressive strength. Good thermal properties. Very low shrinkage: include 0,5% on average for the design of the mold. Low coefficient of linear expansion. High dimensional stability.UL classification: UL94 HB (3,05mm) RTI(C) 110/105/110Example applications: Quick connectors.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English
Density	1.24 g/cc	0.0448 lb/in³
Water Absorption	1.2 %	1.2 %
Melt Flow	4.8 g/10 min @Load 2.16 kg, Temperature 235 °C	4.8 g/10 min @Load 4.76 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	112 MPa	16200 psi	5 mm/min
Elongation at Break	5.0 %	5.0 %	5 mm/min
Tensile Modulus	8.00 GPa	1160 ksi	1 mm/min

Thermal Properties	Metric	English	Comments
Melting Point	174 °C	345 °F	10°C/min
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.10 mm	HB @Thickness 0.122 in

Electrical Properties	Metric	English
Dielectric Strength	35.5 kV/mm	902 kV/in
Dissipation Factor	0.000345 @Frequency 1e+6 Hz	0.000345 @Frequency 1e+6 Hz
	0.00040 @Frequency 100 Hz	0.00040 @Frequency 100 Hz
Comparative Tracking Index	600 V	600 V