Nilit Nilamid B G6 FR C4 30% Glass Fiber Reinforced, Flame Retardant PA6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Nilit |
| Trade Name | Nilamid |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit Nilamid B G6 FR C4 30% Glass Fiber Reinforced, Flame Retardant PA6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Nilamid B G6 FR C4 combines excellent mechanical performance with flame retardancy. The halogenated flame retardant system used in this product allows a wide range of colors. This product does not contain the flame retardants mentioned in the WEEE directive (PBB or PBDE). The product is used widely throughout the electrical and appliance industries for applications like pressure switches, circuit breaker housings, contactors, timers and programmers.Key characteristics: UL listed V0 at 3.0 and 0.75 mmUL listed GWIT 825 °C and GWFI 960°C at 0.75 mm, compliant with IEC 60335-4UL listed on CTI PCL 1 (CTI = 425 V)Excellent mechanical performanceColorable in light colorsEasy processing Information provided by NILIT.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 1.3 % | 1.3 % | 23°C, 24h in H<sub>2</sub>O; sim. ISO 62 |
| Water Absorption at Saturation | 5.0 % | 5.0 % | sim. ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | Euronil |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | Euronil |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 130 MPa | 18900 psi | ISO 527, ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527, ASTM D638 |
| Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527, ASTM D638 |
| Flexural Yield Strength | 190 MPa | 27600 psi | ISO 178, ASTM D790 |
| Flexural Modulus | 8.60 GPa | 1250 ksi | ISO 178, ASTM D790 |
| 4.20 GPa @Temperature 90.0 °C |
609 ksi @Temperature 194 °F |
ISO 178, ASTM D790 | |
| Izod Impact, Notched (ISO) | 6.50 kJ/m² @Temperature -30.0 °C |
3.09 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 8.00 kJ/m² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Charpy Impact Unnotched | 2.80 J/cm² | 13.3 ft-lb/in² | ISO 179 |
| 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 |
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 120 °C | 248 °F | 20,000 hr; IEC 216 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75, ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | ISO 75, ASTM D648 |
| Vicat Softening Point | 190 °C | 374 °F | 49 N; ISO 306, ASTM D1525 |
| 210 °C | 410 °F | 9.8 N; ISO 306, ASTM D1525 | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
||
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Oxygen Index | 33 % | 33 % | ASTM D2863 |
| Glow Wire Test | 960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
Glow Wire Flammability Index; IEC 694-2-12 |
| 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
Glow Wire Flammability Index; IEC 694-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 21.0 kV/mm @Thickness 2.00 mm |
533 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Comparative Tracking Index | 275 V @Thickness 3.20 mm |
275 V @Thickness 0.126 in |
Sol. B; IEC 112, UL 746A |
| 425 V @Thickness 3.20 mm |
425 V @Thickness 0.126 in |
Sol. A; IEC 112, UL 746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Nozzle Temperature | 245 - 275 °C | 473 - 527 °F | |
| Zone 1 | 240 - 260 °C | 464 - 500 °F | hopper |
| Zone 2 | 240 - 265 °C | 464 - 509 °F | |
| Zone 3 | 240 - 270 °C | 464 - 518 °F | |
| Zone 4 | 245 - 275 °C | 473 - 527 °F | |
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | Do not melt above 280°C |
| Mold Temperature | 90.0 - 110 °C | 194 - 230 °F | Preferred |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 70.0 - 100 MPa | 10200 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clamping Force | in tons, 0.7 times the projected surface area in cm2 | |
| Flammability Rating | SE | FMVSS No. 302, 355x100x1 mm |
| Heat Resistance - Ball Test | OK | at 125°C, IEC 309 |
| OK | at 165°C, IEC 309 | |
| Holding Pressure | 90 MPa | |
| Needle Test | OK | IEC 695-2-2, 1 or 2 mm |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 905 PC Copolymer (Asia Pacific)
- SABIC Innovative Plastics Lexan® OQ2720 PC (Asia Pacific)
- Zircar Zirconia ZYZ-3 Zirconia Boards and Discs Insulation
- Resinlab® CYNERGY CA6208 Adhesive
- Techmer ES Luriblend® PC IM FR
- Borealis Borcoat™ BB127E Polypropylene Adhesive Powder form for Steel Pipe Coating
- A. Schulman PP 1259 Polypropylene Medium Impact Polypropylene
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 83A
- Albis Plastics Cellulose Acetate Butyrate B902 (UV Inhibitor Added), 10% Plasticizer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved