Sax Polymers SAXAMID 126F5 Nylon 6, 25% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 126F5 Nylon 6, 25% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 126F5 is a polyamide 6 injection-molding-grade reinforced with 25% glass fibers.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 160 MPa | 23200 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 8.00 GPa | 1160 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 265 MPa | 38400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.50 GPa | 943 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 77.0 kJ/m² @Temperature 23.0 °C |
36.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 6.80 J/cm² @Temperature -30.0 °C |
32.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 7.50 J/cm² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 209 °C | 408 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 214 °C | 417 °F | B/120; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- Karina 40/447-FC-LMP Green Color Concentrate for PVC
- Teknor Apex Monprene® MP-1775B Thermoplastic Elastomer
- A. Schulman POLYBATCH™ White P8555 SD Concentrate Based In Homopolymer Polypropylene
- Lubrizol ESTANE® 58866 Ether Based Thermoplastic Polyurethane
- Loctite® 493 General Purpose Methyl Cyanoacrylate Bonding Adhesive
- Chesterton ARC 5 Paste grade Rapid Cure Abrasion Control
- EMS-Griltech Grilon® M 371 White Nylon 6 Fiber
- 3M 7014FP Performance Paper Label Material
- Chevron Phillips HiD® 9512/HiD® 9513 with Antistat HDPE Blow Molding Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved