BASF Capron® 8360 HS 34% Mineral-Filled Nylon 6 (Conditioned)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® 8360 HS 34% Mineral-Filled Nylon 6 (Conditioned)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Capron 8360 HS is a heat stabilized 34% mineral reinforced nylon 6 injection molding resin possessing a high level of toughness and ductility combined with excellent processability and surface aesthetics. Its performance characteristics include strength and stiffness while maintaining excellent drop weight impact. It maintains its inherent chemical resistance to greases, oils and hydrocarbons. It is also available in natural, black or custom colors and can be painted.Capron 8360 HS is generally recommended for applications such as automotive fuel filter pockets, door and window hardware, wheel hubs and covers, mirror housings, and interior lighting components. ASTM Callout PA220 M34 A92120 UB041 AA002 ZP01 NNI > = 1600 J/M.Data provided by Allied Signal.Processing: Max. water content 0.12%. Product is supplied in sealed containers and drying is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 85°C (185 °F). Is recommended. Drying time is dependent on moisture level.Melt Temperature: 270-300 degC (518-572 degF). Mold Temperature: 80-95 degC (176-203 degF). Injection and Packing Pressure: 35-125 bar (500-1500psi) This product can be processed over a wide range of mold temperatures; however, for applications where aesthetics critical, a mold surface temperature of 80-95 degC (176-203 degF) is required. Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off. Back pressure can be utilized to provide uniform melt consistency and reduce trapped air and gas. A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate. Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
(Dry)
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
ASTM Data MD (Dry)
Mechanical Properties Metric English Comments
Tensile Strength, Yield 50.0 MPa
7250 psi
ASTM test; 50 mm/min.
Elongation at Break >= 50 %
>= 50 %
Nominal
Flexural Yield Strength 70.0 MPa
10200 psi
ASTM Data
Flexural Modulus 2.14 GPa
310 ksi
ASTM Data
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
(Dry)
Processing Properties Metric English Comments
Drying Temperature 85.0 °C
185 °F
See Materials Notes