Lanxess Pocan® DP C 1502 702353 PBT+PC (discontinued **)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® DP C 1502 702353 PBT+PC
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT+PC, non-reinforced, injection molding, impact modified, low tendency to warp, UV-stabilized
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.237 g/cc | 0.04469 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0011 cm/cm | 0.0011 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0011 cm/cm | 0.0011 in/in | ISO 294-4, 2577 |
| Melt Flow | 37 g/10 min @Load 5.00 kg, Temperature 270 °C |
37 g/10 min @Load 11.0 lb, Temperature 518 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527-1/-2 |
| Elongation at Yield | 3.8 % | 3.8 % | ISO 527-1/-2 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527-1/-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 219 °C | 426 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets | |
| ISO Shortname | ISO 7792-1-PBT+PC,GHLMPR,11-020 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- PolyOne Nymax™ GF 600 A 33 Black 13 Polyamide 6 (Nylon 6)
- Gouda Vuurvast CURON 160 H SIC GM Dense Refractory Castable
- Ferro IP 550 Thick Film Glass
- Ineos N00M-00 Polypropylene Impact Copolymer
- Formosa Plastics Formolene® 2550A Thin Walled Injection Molding Polypropylene
- Wanhua Chemical Wanthane® WHT-1485RV Polyester Based TPU
- Ensinger Tecamid® 6/6 Nylon (PA66)
- ExxonMobil Paxon™ FD60-018 Compression Molding Resin
- DuPont Teijin Films Mylar® E Polyester Film, 92 Gauge
- Eurostar Starflam RF0023E PA66/6, 10% Glass Filled, Injection Molded