- Clariant Renol PA1SP0003 Nylon 66, PE Modified
Clariant Renol PA1SP0003 Nylon 66, PE Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PA1SP0003 Nylon 66, PE Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Reduced Coefficient of FrictionData provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 15 % | 15 % | ISO 527 |
| Flexural Modulus | 2.05 GPa | 297 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.50 kJ/m² | 1.67 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 65.6 - 79.4 °C | 150 - 175 °F | |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® OQ1022 PC (Asia Pacific)
- Overview of materials for Polystyrene, Wood Filled
- Minelco Aggregates
- A. Schulman POLYBATCH™ Blue 4656 Concentrate Based In Polyethylene
- Cossa Polimeri ESTABLEND 0840 GF Polycarbonate ABS Blend, 20% Glass Filled
- Adell EZ-14 Homopolymer Polypropylene, 20% Calcium Carbonate Filled
- Ascend Performance Materials Vydyne® R525H BLK Nylon 66, 25% Glass Reinforced, Conditioned
- Beijing Evergrow Resources ER-25 UHMW PE and Ceramic Composite Plate
- Matrixx Group 80M7451 45% Glass/Mineral Filled PET (discontinued **)
Copyright © lookpolymers.com All Rights Reserved