Polyram RamLloy PBB702 PC/ABS alloy, UV Stabilized
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamLloy PBB702 PC/ABS alloy, UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
UV stabilized PC/ABS alloy for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DIN 53479 |
| Moisture Absorption at Equilibrium | 8.0 % | 8.0 % | DIN 53714 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | |
| Melt Flow | 9.0 g/10 min @Load 5.00 kg, Temperature 240 °C |
9.0 g/10 min @Load 11.0 lb, Temperature 464 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM-D638 |
| Elongation at Break | 40 % | 40 % | ASTM-D638 |
| Tensile Modulus | 1.80 GPa | 261 ksi | ASTM-D790 |
| Flexural Strength | 80.0 MPa | 11600 psi | ASTM-D790 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ASTM-D790 |
| Izod Impact, Notched | 5.00 J/cm @Temperature 23.0 °C |
9.37 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | DIN 53461 |
| Vicat Softening Point | 120 °C | 248 °F | ASTM-D1525 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | DIN 53482 |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH GF5020 PD1 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- Polymer Resources AH-GP1 Acetal Homopolymer, Low Flow, High Melt Strength, Heat Stabilized
- Arlon A1030-R008-12 0.030" (0.762 mm) Fully Cured Fusible Silicone Rubber - Extruded Fusible Tape (disco
- Haynes Hastelloy® C-22® alloy, 20% cold worked sheet
- Solvay TECHNYL® A 218 V35 PA66, 35% glass fiber, DRY
- A. Schulman POLYBATCH™ Navajo 10294U/4 Concentrate Based In LLDPE
- DuPont Performance Polymers Zytel® 7301 NC010 Nylon 6 (Unverified Data**)
- Beijing Chemical Industry KAIFA® MN301-G35 Nylon 66 Resin
Copyright © lookpolymers.com All Rights Reserved