Shanghai Ofluorine M-1 PVDF Molding Grade

Category	Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded
Manufacturer	Shanghai Ofluorine
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Shanghai Ofluorine M-1 PVDF Molding Grade.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: M-1 PVDF is a kind of granules homopolymer, which has high melt viscosity, M-1 is more suitable for compression molding process. M-1 PVDF pellets as raw materials, the finished products has excellent mechanical strength and tenacity. It can not be eroded by acid, alkali, strong oxidant, halogens. Good durability to aliphatic hydrocarbons, aromatic hydrocarbons, alcohol, aldehyde etc. In the work of hydrochloric acid, nitric acid, sulfuric acid, dilute alkali liquor, dense alkali liquor (40%) and 100Â°C temperature, its performance keep stable. Others, M-1 PVDF finished products has the properties of ?-Ray resistant, UV resistant, and stability in wide temperature range.Information provided by Shanghai Ofluorine Chemical Technology

Physical Properties	Metric	English	Comments
Specific Gravity	1.77 - 1.79 g/cc	1.77 - 1.79 g/cc	ASTM D792
Water Absorption	<= 0.050 %	<= 0.050 %	ASTM D570
Melt Flow	1.0 - 4.0 g/10 min @Load 10.0 kg, Temperature 230 Â°C	1.0 - 4.0 g/10 min @Load 22.0 lb, Temperature 446 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	70 - 80	70 - 80	ASTM D2240
Tensile Strength at Break	>= 30.0 MPa	>= 4350 psi	50mm/min; ASTM D638
Tensile Strength, Yield	>= 40.0 MPa	>= 5800 psi	50mm/min; ASTM D638
Elongation at Break	>= 20 %	>= 20 %	50mm/min; ASTM D638
Elongation at Yield	5.0 - 10 %	5.0 - 10 %	50mm/min; ASTM D638

Thermal Properties	Metric	English	Comments
Melting Point	165 - 171 Â°C	329 - 340 Â°F	10Â°C/min; ASTM D3418
Flammability, UL94	V-0	V-0

Descriptive Properties	Value	Comments
Appearance	White translucent pellets