SABIC Innovative Plastics Valox® V2105U PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® V2105U PBT.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Unreinforced, Wear resistant, UV Stabilized PBT designed for outdoor, agricultural, industrial and automotive applications. This grade has very high impact strength to stiffness ratio.
Physical Properties Metric English Comments
Specific Gravity 1.28 g/cc
1.28 g/cc
ASTM D792
Density 1.28 g/cc
0.0462 lb/in³
ISO 1183
Moisture Absorption 0.0800 %
0.0800 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.34 %
0.34 %
ISO 62
Linear Mold Shrinkage, Flow 0.029 - 0.034 cm/cm

@Thickness 3.20 mm
 0.029 - 0.034 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.025 - 0.030 cm/cm

@Thickness 3.20 mm
 0.025 - 0.030 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 9.5 g/10 min

@Load 5.00 kg,
Temperature 266 °C
 9.5 g/10 min

@Load 11.0 lb,
Temperature 511 °F
 ASTM D1238
Melt Index of Compound 8.0 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 8.0 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 52.0 MPa
7540 psi
50 mm/min; ISO 527
58.0 MPa
8410 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 39.0 MPa
5660 psi
Type I, 50 mm/min; ASTM D638
40.0 MPa
5800 psi
50 mm/min; ISO 527
Elongation at Break 230 %
230 %
50 mm/min; ISO 527
300 %
300 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 6.0 %
6.0 %
50 mm/min; ISO 527
17 %
17 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.50 GPa
363 ksi
5 mm/min; ASTM D638
2.54 GPa
368 ksi
1 mm/min; ISO 527
Flexural Yield Strength 62.0 MPa
8990 psi
2 mm/min; ISO 178
65.0 MPa
9430 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 1.87 GPa
271 ksi
2 mm/min; ISO 178
2.06 GPa
299 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 11.6 J/cm
21.7 ft-lb/in
ASTM D256
1.50 J/cm

@Temperature -30.0 °C
 2.81 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 98.0 kJ/m²
46.6 ft-lb/in²
80*10*4; ISO 180/1A
15.0 kJ/m²

@Temperature -30.0 °C
 7.14 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 9.00 J/cm²
42.8 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 63.0 J

@Temperature 23.0 °C
 46.5 ft-lb

@Temperature 73.4 °F
 ASTM D3763
75.0 J

@Temperature -40.0 °C
 55.3 ft-lb

@Temperature -40.0 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 44.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 44.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 120 µm/m-°C

@Temperature -40.0 - 40.0 °C
 66.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
120 µm/m-°C

@Temperature -40.0 - 40.0 °C
 66.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 47.0 °C
117 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
49.0 °C

@Thickness 3.20 mm
 120 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 158 °C
316 °F
Rate B/50; ISO 306
158 °C
316 °F
Rate B/120; ISO 306
158 °C
316 °F
Rate B/50; ASTM D1525