Arkema Group Orgalloy® LE60 THM Polyamide Alloy
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Arkema |
| Trade Name | Orgalloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Orgalloy® LE60 THM Polyamide Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide Alloy, Semi-Flexible gradeTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO R1183 |
| Water Absorption | 0.80 % | 0.80 % | 23°C / 24 hrs; ISO 62 |
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 23°C / 50% RH; ISO 62 |
| 6.0 % | 6.0 % | in 23°C water; ISO 62 | |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
after drying; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 72 | 72 | ISO 868 |
| Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ISO R527 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO R527 |
| Elongation at Break | 300 % | 300 % | ISO R527 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO R527 |
| Modulus of Elasticity | 1.75 GPa | 254 ksi | ISO R527 |
| Flexural Strength | 40.0 MPa | 5800 psi | After conditioning at 23°C and 50% RH; ISO 178 |
| Flexural Modulus | 1.40 GPa | 203 ksi | After conditioning at 23°C and 50% RH; ISO 178 |
| Charpy Impact, Notched | 2.30 J/cm² | 10.9 ft-lb/in² | After conditioning at 23°C/50%RH; ISO 179/Af |
| 2.20 J/cm² @Temperature -20.0 °C |
10.5 ft-lb/in² @Temperature -4.00 °F |
After conditioning at 23°C/50%RH; ISO 179/Af | |
| Tensile Creep Modulus, 1 hour | 1520 MPa | 220000 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ISO R1218 |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ISO R75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO R75 |
| Vicat Softening Point | 204 °C | 399 °F | 10 N - A method; ISO 306 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 |
Users viewing this material also viewed the following:
- Network Polymers PC-1035
- SABIC Innovative Plastics Lexan® CFR5630D PC COPOLYMER (Asia Pacific)
- Haynes Hastelloy® C-22® alloy, SMAW weld, 316L base metal, C-22 weld metal
- Solvay TECHNYL® C 442 Black V PA6, Conditioned
- A. Schulman POLYBATCH™ Brown 1028 Concentrate Based In Polyethylene
- Polyram PlusTek PA301G2 Nylon 6.6 for Injection Molding, 10% Glass Fiber Reinforced, Heat Stabilized
- ExxonMobil Mobil Pegasus 15W-40 40
- Asahi Kasei Leona® 1500 Nylon 66
- Westlake Epolene® N-11 Nonemulsifiable - Low Molecular Weight Polyethylene Polymer
- Arlon R37806X030 Silicone Rubber/Fiberglass
Copyright © lookpolymers.com All Rights Reserved