Lanxess Durethan® DP BM 410 H2.0 901510 Nylon 6, 10% Mineral + Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP BM 410 H2.0 901510 Nylon 6, 10% Mineral + Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, injection molding grade, 10% glass fibers/mineral, good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.206 g/cc | 0.04357 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00124 cm/cm | 0.00124 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0011 cm/cm | 0.0011 in/in | ISO 294-4, 2577 |
| Melt Flow | 43 g/10 min @Load 2.16 kg, Temperature 270 °C |
43 g/10 min @Load 4.76 lb, Temperature 518 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | Conditioned; ISO 527-1/-2 |
| 75.0 MPa | 10900 psi | ISO 527-1/-2 | |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | Conditioned; ISO 527-1/-2 |
| 80.0 MPa | 11600 psi | ISO 527-1/-2 | |
| Elongation at Break | 8.0 % | 8.0 % | ISO 527-1/-2 |
| 183 % | 183 % | Conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 3.5 % | 3.5 % | ISO 527-1/-2 |
| 22.6 % | 22.6 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 1.34 GPa | 194 ksi | Conditioned; ISO 527-1/-2 |
| 4.06 GPa | 589 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 500 V | 500 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6,MHR,040-14,MD10 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® ThinStik Soft Seal 15-06021 Self-Adhesive Urethane Foam
- Premix Thermoplastics PRETECH Halogen-free Engineering Thermoplastics
- Quadrant EPP Proteus® PP, Black Homopolymer Polypropylene (ASTM Product Data Sheet)
- Hong Kun Group 4-tert-Butyl-2,6-diisopropylphenol Pharmaceutical Intermediate
- Techmer ES HiFill® PP GF20 CC HS 20% Glass Filled
- SABIC Innovative Plastics LNP THERMOCOMP UCF26AS PPA (Asia Pacific)
- Solvay SIPOMER® PAM-200 Phosphate Esters of Ppg Monomethacrylate
- Loctite® 3525 Acrylic Light Cure Adhesive
- Chosun Refractories SM-A Special Mortar for Sliding Gate Valve
Copyright © lookpolymers.com All Rights Reserved