LyondellBasell Higlass SB224-1 Polypropylene Copolymer, 10% Glass Fiber

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	LyondellBasell
Trade Name	Higlass
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LyondellBasell Higlass SB224-1 Polypropylene Copolymer, 10% Glass Fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Key Features: conventional melt flow, medium modulus, chemically coupled, glass fiber-reinforced polypropylene copolymer, excellent impact strength, good processabilityApplications: automotive wheel well housings, lawn equipment housings, recreational vehicle partsDescription: Higlass SB224-1 conventional melt flow, chemically coupled, 10% glass fiber-reinforced polypropylene copolymer has an excellent balance of strength, stiffness and impact resistance.Information provided by Montell Polyolefins.LyondellBasell is the successor company to Montell.

Physical Properties	Metric	English	Comments
Density	0.960 g/cc	0.0347 lb/inÂ³	ASTM D792
Linear Mold Shrinkage	0.0060 cm/cm	0.0060 in/in	Tool, Montell
Melt Flow	6.0 g/10 min @Load 2.16 kg, Temperature 230 Â°C	6.0 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	36.0 MPa	5220 psi	ASTM D638
Elongation at Break	9.0 %	9.0 %	ASTM D638
Flexural Modulus	1.60 GPa	232 ksi	Tangent at 0.05 in/min; ASTM D790A
Izod Impact, Notched	1.70 J/cm	3.18 ft-lb/in	ASTM D256A
Izod Impact, Unnotched	5.30 J/cm	9.93 ft-lb/in	ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	148 Â°C	298 Â°F	ASTM D648
UL RTI, Mechanical with Impact	115 Â°C @Thickness 1.60 mm	239 Â°F @Thickness 0.0630 in
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in