Menzolit Menzolit® BMC 0390 Unsaturated Polyester UP
| Category | Polymer , Thermoset , Polyester, TS , Thermoset Polyester Glass Filled BMC |
| Manufacturer | Menzolit |
| Trade Name | Menzolit® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Menzolit Menzolit® BMC 0390 Unsaturated Polyester UP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
BMC 0390 is a low profile DMC/BMC. Because of its low shrinkage, the material shows good surface quality as well as very low warpage. The product is suitable for applications if a better surface quality is necessary that cannot be achieved with low shrink material. Because of the low shrinkage, tool design is more difficult and the user should take care to allow proper part ejection from mould. Typical applications are housings or covers that call for improved surface quality and dimensional stability. Because of this painting may be desired. Paint adhesion of appropriate paint systems is very good. Chrome plating of punch and cavity surfaces is recommended.Information Provided by Menzolit
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 g/cc | 0.0686 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.50 % | <= 0.50 % | ISO 62 |
| Linear Mold Shrinkage | -0.000300 cm/cm | -0.000300 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 36.0 MPa @Temperature 22.0 °C |
5220 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Tensile Strength, Yield | 36.0 MPa @Temperature 22.0 °C |
5220 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Elongation at Yield | 0.00 % | 0.00 % | tensile rupture strain; ISO 527-4 |
| Modulus of Elasticity | 14.0 GPa | 2030 ksi | 25mm flat samples, compression moulded; ISO 527-4 |
| Flexural Strength | 120 MPa @Temperature 22.0 °C |
17400 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Flexural Modulus | 11.0 GPa @Temperature 22.0 °C |
1600 ksi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 5.40 GPa | 783 ksi | in plane |
| Charpy Impact, Notched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | |
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 165 °C | 329 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 150 °C | >= 302 °F | ISO 75-2 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Glass Transition Temp, Tg | 170 °C | 338 °F | ISO 11357-2 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Oxygen Index | 22 % | 22 % | ISO 4589-2 |
| Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 4.0 | 4.0 | IEC 60250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 160 °C | 275 - 320 °F | Injection moulding, matched metal die |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hysun™ 678UV ASA
- PolyOne Edgetek® PI-30GF/000 Polyether Imide (PEI)
- PolyOne Geon™ HC 2185G Polyvinyl Chloride, Flexible (PVC, Flexible)
- H.C. Starck Pure Molybdenum ABL, Arc-Cast, Low Carbon Bar
- Gouda Vuurvast CURON 150 HR GM Dense Refractory Castable
- SABIC Innovative Plastics LNP THERMOCOMP LC008E PEEK
- Solvay RHODOLINE® 622 Surfactant
- Epoxyset Epoxibond EB-135 Unfilled Epoxy Adhesive
- 3M 471+ Vinyl Tape
- Pyrotek Mesh core / V-5 Tadpoles
Copyright © lookpolymers.com All Rights Reserved