SABIC Innovative Plastics SABIC PPCOMPOUND 19T1020 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | SABIC PPCOMPOUND |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics SABIC PPCOMPOUND 19T1020 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SABIC® PPcompound 19T1020 is a general purpose, talc filled, heat stabilized homopolymer polypropylene compound. This compound exhibits high flow and is suitable for injection molding applications. The IMDS ID is 163255030.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 230 °C |
18 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 74 | 74 | ISO 868 |
| Tensile Strength at Break | 29.0 MPa | 4210 psi | Type I, 50 mm/min; ASTM D638 |
| 32.0 MPa | 4640 psi | 50 mm/min, 1A; ISO 527 | |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50 mm/min; ISO 527 |
| 36.0 MPa | 5220 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 10.6 % | 10.6 % | 50 mm/min; ISO 527 |
| 20.5 % | 20.5 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.5 % | 4.5 % | 50 mm/min; ISO 527 |
| 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.97 GPa | 431 ksi | 50 mm/min; ASTM D638 |
| 3.20 GPa | 464 ksi | 1 mm/min; ISO 527 | |
| Flexural Modulus | 2.49 GPa | 361 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.17 GPa | 460 ksi | 2 mm/min, 64mm span; ISO 178 | |
| Izod Impact, Notched | 0.210 J/cm | 0.393 ft-lb/in | 63.5*12.7*3.2mm, Cut; ASTM D256 |
| Izod Impact, Unnotched | 4.10 J/cm | 7.68 ft-lb/in | 63.5*12.7*3.2mm, Cut; ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4mm, Cut; ISO 180/1A |
| 1.00 kJ/m² @Temperature -30.0 °C |
0.476 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 180/1A | |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | 80*10*4mm, Cut; ISO 179/1eA |
| 0.100 J/cm² @Temperature -30.0 °C |
0.476 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 179/1eA | |
| Dart Drop, Total Energy | 3.00 J @Temperature 23.0 °C |
2.21 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak, 6.6 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 58.0 µm/m-°C @Temperature -30.0 - 100 °C |
32.2 µin/in-°F @Temperature -22.0 - 212 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 115 µm/m-°C @Temperature -30.0 - 100 °C |
63.9 µin/in-°F @Temperature -22.0 - 212 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C | 262 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| 129 °C @Thickness 3.20 mm |
264 °F @Thickness 0.126 in |
ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.0 °C | 163 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| 73.0 °C @Thickness 3.20 mm |
163 °F @Thickness 0.126 in |
ASTM D648 | |
| Vicat Softening Point | 157 °C | 315 °F | 10N, 50°C/hr; ISO 306 |
Users viewing this material also viewed the following:
- LG Chemical Lupoy 1303-10 Polycarbonate Resin
- H.C. Starck Amperit® 782.054 Titanium Oxide (TiO2)
- SABIC Innovative Plastics LNP THERMOCOMP DF004 PC (Europe-Africa-Middle East)
- Chase Plastics CP Pryme® PC100RHF Polycarbonate
- A. Schulman POLYBATCH™ Yellow P20199/2 Concentrate Based In Copolymer PP
- Epoxy Technology EPO-TEK® 730 General Purpose Epoxy
- Fainplast Compounds FR 91 Flexible PVC, Insulation
- Vyncolit W5020 Glass Filled Novolac Phenolic
- Amco PRIMATOP HDPE 003955PZ Phillips Process Hexene Copolymer
Copyright © lookpolymers.com All Rights Reserved