Aclo Accutech Polypropylene Homopolymer HP0336T20L1 Talc Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0336T20L1 Talc Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | MD; ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Ash | 25 % | 25 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Elongation at Break | 16 % | 16 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 1.700 GPa | 246.5 ksi | ASTM D638 |
| Flexural Strength | 49.0 MPa | 7110 psi | ASTM D790 |
| Flexural Modulus | 2.499 GPa | 362.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.299 J/cm | 0.560 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F |
Users viewing this material also viewed the following:
- ExxonMobil Escorene® LD-722 High EVA Film and Compounding Resin (discontinued **)
- Lubrizol Advanced Materials Pearlstick® 45-90/06 Polycaprolactone based TPU
- A. Schulman LB502-01 High Molecular Weight, High-Density Polyethylene Copolymer
- A. Schulman LP552-01 Narrow Molecular Weight Copolymer, High-Density Polyethylene
- EMS-Grivory Grivory® TSM-40/4 PA666-MD40
- Ensinger Tecatron® XP-64 Compression Molded PPS Compound, 40% Fiberglass
- Dow CYRACURE™ UVR-6110 Cycloaliphatic Epoxide
- Bulk Molding Compounds BMC 501 Mineral Filled, Glass Fiber Reinforced Compound
- DuPont Performance Polymers VTR 8500 (GLT-S) 8500 Peroxide Cured Fluoroelastomer (FKM) Formulation (discontin
Copyright © lookpolymers.com All Rights Reserved