Nylacast Cast Nylon 6, Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | Nylacast |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nylacast Cast Nylon 6, Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Nylacast Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | method A; ISO 1183:1987 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 - 70.0 MPa | 8700 - 10200 psi | Type 1B, 50mm/min; ISO 527-1/2:1993 |
| Elongation at Break | >= 10 % | >= 10 % | Type 1B, 50mm/min; ISO 527-1/2:1993 |
| Tensile Modulus | 3.00 GPa | 435 ksi | Type 1B, 50mm/min; ISO 527-1/2:1993 |
| Flexural Strength | 95.0 MPa | 13800 psi | 1.5mm/min; ISO 178:2001 |
| Flexural Modulus | 2.70 GPa | 392 ksi | 1.5mm/min; ISO 178:2001 |
| Compressive Strength | 130 MPa | 18900 psi | Type B, 5mm/min; ISO 604:2002 |
| Compressive Modulus | 2.60 GPa | 377 ksi | Type B, 5mm/min; ISO 604:2002 |
| Izod Impact, Notched (ISO) | 5.60 kJ/m² | 2.66 ft-lb/in² | Type A; ISO 180:2000 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-2:1999 |
| Melting Point | 225 °C | 437 °F | |
| Maximum Service Temperature, Air | 190 °C | 374 °F | Intermittent |
| 120 °C @Time 1.80e+7 sec |
248 °F @Time 5000 hour |
Continuous | |
| Minimum Service Temperature, Air | -100 °C | -148 °F | Intermittent |
| -40.0 °C | -40.0 °F | Continuous |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093:1980-01 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093:1980-01 |
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 60250:1969-01 |
| 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
IEC 60250:1969-01 | |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243-1:1998-01 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112:2003-01 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black |
Users viewing this material also viewed the following:
- Oxford Polymers Oxnilon 6-14GF 14% Glass Fiber Filled Nylon 6 for Injection Molding
- LATI Latene® 7 TR-V2 PP Homopolymer, Mineral Reinforced, Flame Retardant
- Polyram Bondyram® TL1207 Maleic Anhydride Modified Co-Polymer Polypropylene
- EMS-Grivory Grivory® LBV-30H FWA nat PA12-GF30
- Arkema Group Nakan® FMM 611 N PVC, Soft Injection Molding Grade
- Plastcom SLOVALEN PH 73 T 20 PP, 20% mineral filling
- A. Schulman POLYFORT™ PP 3052UX Impact Resistant Copolymer
- Borealis Daplen™ KB4436 TPO Compound
- LNP Lubricomp® OCL-4536 Polyphenylene Sulfide, Carbon Fiber Reinforced, PTFE + Silicone Lubricant (discontinu
Copyright © lookpolymers.com All Rights Reserved