Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 89.6 MPa | 13000 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Gravi-Tech™ GRV-NY-035-SS-GF-BLK Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
Oxford Polymers 15GF 15% Glass Fiber Reinforced Polybutylene Terephthalate (PBT) 15% Glass Fiber Reinforced Polybutylene Terephthalate (PBT)Information provided by Oxford Polymers. |
|||
Tensile Strength, Yield | 89.6 MPa @Thickness 3.17 mm |
13000 psi @Thickness 0.125 in |
|
Nilit Polynil® N66-P50N Lubed Nylon 6/6 Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
Tensile Strength, Yield | 89.6 MPa @Temperature 23.9 °C |
13000 psi @Temperature 75.0 °F |
0° Direction, Dry; 325°F Autoclave; ASTM D638 |
Park Electrochemical Nelcote® F-557 Phenolic Prepreg, Aerospace Silica Fabric Reinforced Nelcote® F-557 is a high purity silica filler phonic resin coated on Commercial or Aerospace grade silica fabric. F-557 is used in the manufacture of intermediate temperature ablative rocket nozzle.. |
|||
Tensile Strength, Yield | 89.6 MPa @Temperature 23.9 °C |
13000 psi @Temperature 75.0 °F |
0° Direction, Dry; 325°F Autoclave; ASTM D638 |
Park Electrochemical Nelcote® F-557 Phenolic Prepreg, Commercial Silica Fabric Reinforced Nelcote® F-557 is a high purity silica filler phonic resin coated on Commercial or Aerospace grade silica fabric. F-557 is used in the manufacture of intermediate temperature ablative rocket nozzle.. |
|||
Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
Polymer Resources TP-G15 Polybutylene Terephthalate, 15% Glass Reinforced Polybutylene Terephthalate, 15% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information prov.. |
|||
Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
Ravago Manufacturing Americas Hylon® N2040ML Nylon 6 (DAM) Information provided by Ravago. |
|||
Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
Fiberfil® J-60/30/E/M Polypropylene Homopolymer, 30% Glass Reinforced, Chemically coupled Information provided by FIBERFIL Engineered Plastics |
|||
Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
Greene Tweed Arlon® 1330 PEEK Arlon® is a tough, high-temperature, semi-crystalline, thermoplastic presenting a unique combination of mechanical, thermal, chemical and electrical properties. Greene, Tweed uses several proprie.. |
|||
Tensile Strength, Yield | 89.66 MPa | 13000 psi | ASTM D638 |
Lucent Polymers GPB-FR515 Polybutylene Terephthalate, 15% Glass Fiber Reinforced, Flame Resistant Add "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc. |
|||
Tensile Strength, Yield | 89.66 MPa | 13000 psi | ASTM D638 |
Lucent Polymers GPP-140 Polypropylene Homopolymer, 40% Glass Fiber Reinforced, Chemically Coupled Melt Flow Adjustable for ApplicationAdd "U" for UV StabilizedAdd "H" for Heat StabilizedInformation provided by Lucent Polymers, Inc. |
|||
Tensile Strength, Yield | 89.6 MPa @Thickness 3.17 mm |
13000 psi @Thickness 0.125 in |
LW |
Industrial Laminates/Norplex MC330 Cotton Fabric Description: Grade MC330 is a cotton cloth/phenolic resin composite which is specially processed to be used in cryogenic applications. Such applications include spacers for installation of liquid ox.. |
|||
Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
Techmer ES Elastoblend® PA6 GF15 IM1 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impac.. |
|||
Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
Techmer ES HiFill FR® PA6/6 GF10 FR HS BK 10% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 10% Filler by WeightAdditive: Heat StabilizerFeatures: Flame Retardant and Heat StabilizedAppearance: BlackTPCI# 9550101In.. |
|||
Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
Techmer ES HiFill® PA6 0135 BL069 13% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 13% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized and LubricatedAppearanc.. |
|||
Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
Techmer ES HiFill® PA6 GF/B20 A2 20% Glass Fiber/Glass Bead Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber/Glass Bead, 20% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedInformation .. |
|||
Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
Techmer ES HiFill® POM CO GF10 CC 10% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforced, 10% Filler by WeightFeatures: Copolymer and Chemically CoupledInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
Techmer ES Luriblend® PA6 ML2 Nylon 6 Availability: North AmericaForms: PelletsAdditive: Molybdenum Disulfide Lubricant(2%)Features: Good Wear Resistance, Low Friction and LubricatedInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
Techmer ES HiFill® PPS 0334 A Availability: North AmericaForms: PelletsFeatures: High DensityInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 89.6 - 152 MPa | 13000 - 22000 psi | 0.2% offset |
Eagle Brass 425 Tin Brass 2%, Annealed Alloy C425 is a low zinc-containing alloy with good combination of tensile strength, electrical conductivity, formability and corrosion resistance. Applications include electrical springs, connector.. |
|||
Tensile Strength, Yield | 89.6 - 172 MPa | 13000 - 25000 psi | 0.2% offset |
Eagle Brass 706 Copper Nickel 10%, Annealed 706 exhibits excellent corrosion resistance, especially in marine applications. It has a relatively high strength and has resistance at elevated temperatures. The cost is relatively high compared to.. |
|||
Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
Clariant Renol PA101F/ST801 Nylon 66, Impact Modified, Lubricated Data provided by Clariant Masterbatches |
|||
Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
Clariant Renol PA113G13X050 Nylon 66, 13% Glass Fiber, Heat Stabilized, Lubricated, Improved Ductility Data provided by Clariant Masterbatches |
|||
Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
Asahi Kasei Thermylene® P6-30FG-0684 30% Glass Fiber Reinforced, Heat and UV Information provided by Asahi Thermofil |
|||
Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
Techmer ES Luriblend® HTN 01410 BK Availability: North AmericaForms: PelletsAdditive: Graphite Powder Lubricant and Molybdenum Disulfide LubricantFeatures: Good Wear Resistance, Low Friction, High Heat Resistance and LubricatedAppear.. |
|||
Tensile Strength, Yield | 89.6 MPa | 13000 psi | Type 1 - Rigids, Break, 0.2 in/min; ASTM D638 |
PolyOne Edgetek® NL-10GF/000 Nylon 6/12, Glass Filled
(discontinued **) Description/Features:Glass Fiber ReinforcedInformation provided by PolyOne Corporation. |
|||
Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
Polymer Resources PPX-G20 Modified PPO, 20% Glass Reinforced
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |