- Ravago Manufacturing Americas Hylon® N2040ML Nylon 6 (DAM)
Ravago Manufacturing Americas Hylon® N2040ML Nylon 6 (DAM)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylon® N2040ML Nylon 6 (DAM).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ASTM D792 |
| Water Absorption | 1.1 % | 1.1 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D638 |
| Flexural Strength | 128 MPa | 18500 psi | ASTM D790 |
| Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.4 µm/m-°C @Temperature 20.0 °C |
28.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 282 °C | 500 - 540 °F | |
| Mold Temperature | 71.1 - 98.9 °C | 160 - 210 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.18 % | 0.18 % | |
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |
| Screw Speed | 50 - 120 rpm | 50 - 120 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure | 750 to 1400 psi | |
| Injection Rate | Fast |
Users viewing this material also viewed the following:
- MetalTek RENE® 220 Centri-Vac Nickel Cobalt Based Alloy
- Teknor Apex Monprene® MP-1657L3 Thermoplastic Elastomer
- Polyram RamTough RZ321G2 Polycarbonate, 10% Glass Fiber, Flame Retardant
- Hexcel® HexForce™ 2116 Fiber Glass Fabric
- A. Schulman PP 2173-01 Polypropylene High-Impact Polypropylene
- Total HDPE HD 6081 High Density Polyethylene - Injection Molding
- Eastman Tritan MX731 Copolyester
- CP-Polymer-Technik Wellamid® 6000/58 HWUVCP Nylon 6, Impact Modified Until -40°C, UV Stabilized, Heat Stabilized, Conditioned
- Azoty Tarnow™ Tarnamid® T-27 CF10 Polyamide 6 10% Carbon Fiber - Antistatic and Electroconductive
- Solvay Specialty Polymers Solef® 60512 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved