Polymer Resources PPX-G20 Modified PPO, 20% Glass Reinforced (Unverified Data**)

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 20% Glass Filled
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources PPX-G20 Modified PPO, 20% Glass Reinforced (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/in³	ASTM D792
Linear Mold Shrinkage	0.0020 - 0.0050 cm/cm	0.0020 - 0.0050 in/in	ASTM D955
Melt Flow	1.0 - 4.0 g/10 min	1.0 - 4.0 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	93.1 MPa	13500 psi	ASTM D638
Tensile Strength, Yield	89.6 MPa	13000 psi	ASTM D638
Flexural Strength	124 MPa	18000 psi	ASTM D790
Flexural Modulus	4.83 GPa	700 ksi	ASTM D790
Izod Impact, Notched	0.801 J/cm	1.50 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	138 °C	280 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	132 °C	270 °F	ASTM D648
Flammability, UL94	HB	HB	1/16 in
	HB	HB	1/8 in

Processing Properties	Metric	English
Rear Barrel Temperature	260 - 304 °C	500 - 580 °F
Middle Barrel Temperature	271 - 310 °C	520 - 590 °F
Front Barrel Temperature	282 - 316 °C	540 - 600 °F
Melt Temperature	288 - 316 °C	550 - 600 °F
Mold Temperature	71.1 - 104 °C	160 - 220 °F
Drying Temperature	104 - 110 °C	220 - 230 °F
Dry Time	3 - 4 hour	3 - 4 hour