- Polymer Property : Tensile Strength, Yield = 79.0 MPa
Polymer Property : Tensile Strength, Yield = 79.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | ASTM D638 |
| NYCOA 870 PA 6 plasticized and heat stabilized extrusion grade for the wire jacketing industry to 3,000 fpm. UL Flammability Component listing for use as cable jacketing.Information provided by NYCOA, Inc. |
|||
| Tensile Strength, Yield | 79.0 - 85.0 MPa | 11500 - 12300 psi | Type 1B, 50mm/min; ISO 527-1/2:1993 |
| Nylacast Moly Cast Nylon 6, MoS2 Filled Nylacast Moly is part of the Cast Nylon 6 family. Its improved crystallization occurs by the addition of Molybdenum Disulphide. It includes MoS2, which is an extremely effective self dry lubricant w.. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP COLORCOMP R1000 PA 66 LNP* COLORCOMP* R1000 is an unfilled Nylon 66. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | 50 mm/min; ISO 527 |
| BASF Capron® 8200 NL Nylon 6 (DAM)
(discontinued **) Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | 2 in/min; ASTM D638 |
| BASF Capron® 8202 NL Nylon 6 (DAM)
(discontinued **) Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | 50 mm/min; ISO 527 |
| BASF Capron® 8224 HSL Nylon 6 (DAM)
(discontinued **) Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON Noryl_HMC1010 PPE+HIPS (Europe-Africa-Middle East) LNP* Stat-kon* HMC1010 compound is a 10% Carbon fiber reinforced. Static dissipative. Nonbrominated, nonchlornated flame retardant system. UL94 V-1 rated. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON Noryl_HMC1010 PPE+PS LNP* Stat-kon* Noryl_HMC1010 compound is a 10% Carbon fiber reinforced. Static dissipative. Nonbrominated, nonchlor- nated flame retardant system. UL94 V-1 rated. |
|||
| Tensile Strength, Yield | 79.0 MPa @Temperature -40.0 °C |
11500 psi @Temperature -40.0 °F |
ISO Data |
| Styrolution Luran® S 777 K ASA Luran S 777 K is an easy flowing injection molding ASA grade with good toughness and heat distorsion resistance. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL NH5020 PPE+PS (Europe-Africa-Middle East) Noryl* NH5020 Resin is an unreinforced blend of Polyphenylene Ether(PPE) + Polystyrenre resin. The material offers a good balance of heat, flow, hydrolytic stability, and non-halogenated flame reta.. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL PPX PPX630 PPE+PP 30% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited). |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL PPX PPX630 PPE+PP (Asia Pacific) 30% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited). |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP NF002 PC+ABS LNP THERMOCOMP* NF002 is a compound based on PC+ABS resin containing 10% Glass Fiber. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP RB004 PA 66 LNP* THERMOCOMP* RB004 is a compound based on Nylon 66 containing Glass Beads. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Noryl 534 PPE+PS High heat, unreinforced.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL EXNL0143 PPE+PS Noryl PX1736 Resin is a blend of PPE and PS, that provides high strength, increased heat resistance, and translucency. The material has melt strenght suitable for Extrusion and Blow Molding applica.. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Noryl GTX APS8740 PPE+PPS Noryl* APS8740 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can be e.. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Noryl GTX APS8740 PPE+PPS (Asia Pacific) Noryl* APS8740 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can be e.. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Noryl GTX APS8740 PPE+PPS (Europe-Africa-Middle East) Noryl* APS8740 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can be e.. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Nominal Stress, yld, Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL GTX EXNX0080 PPE+PPS (Asia Pacific) Noryl APS* EXNX0080 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can.. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Nominal Stress, yld, Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL GTX EXNX0080 PPE+PPS (Europe-Africa-Middle East) Noryl APS* EXNX0080 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can.. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL PX1736 PPE+PS Noryl PX1736 Resin is a blend of PPE and PS, that provides high strength, increased heat resistance, and translucency. The material has melt strenght suitable for Extrusion and Blow Molding applica.. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | 2 in/min; ASTM Test |
| BASF Ultramid® 8202 HS PA6 (Dry) Ultramid 8202 HS is a heat stabilized, low viscosity, general purpose nylon 6 injection molding homopolymer. It possesses the combination of strength and toughness and has excellent chemical and ab.. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | 2 in/min; ASTM Test |
| BASF Ultramid® 8202 PA6 (Dry) Ultramid 8202 is a low viscosity, general purpose polyamide 6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is also available in heat stabilized (Ult.. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | 50mm/min; ISO 527 |
| BASF Ultramid® B3S Q661 PA6 (Dry) Ultramid B3S Q661 is a general purpose, PA6 resin for injection molding. |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Dry; ASTM D638 |
| Asahi Kasei Leona® 1300S Nylon 66 General purpose grade. Good balance of flowability and mechanical properties.Applications:Connectors, washers, cable ties. Information provided by Asahi Kasei |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Wet; ASTM D638 |
| Asahi Kasei Leona® 14G15 15% Glass Filled Nylon 66 15% Glass Fiber Reinforced. Enhanced strength and stiffnessApplications:Heater tanks, fuel injectors, ABS sensors, and other under-the-hood automotive parts Information provided by Asahi Kasei |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Dry; ASTM D638 |
| Asahi Kasei Leona® 1502 Nylon 66 Similar to 1500 but with improved heat aging resistance.Applications:Under-the-hood automotive parts Information provided by Asahi Kasei |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Dry; ASTM D638 |
| Asahi Kasei Leona® 9400S Nylon 66 Excellent impact resistance. Suitable for thick-wall parts.Applications:Railroad tie insulatorsInformation provided by Asahi Kasei |
|||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | ASTM D638 |
| Ashley Polymers Ashlene® 835 Nylon 6 Basic Nylon 6 high viscosity, for coating and laminating applications, FDA approved.Data provided by the manufacturer |
|||