SABIC Innovative Plastics NORYL PX1736 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PX1736 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl PX1736 Resin is a blend of PPE and PS, that provides high strength, increased heat resistance, and translucency. The material has melt strenght suitable for Extrusion and Blow Molding applications. Typical applications include High Performance Applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.25 % | 0.25 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 25.1 g/10 min @Load 5.00 kg, Temperature 300 °C |
25.1 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 26 g/10 min @Load 5.00 kg, Temperature 300 °C |
26 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.0 MPa | 8120 psi | Type I, 50 mm/min; ASTM D638 |
| 72.0 MPa | 10400 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | 50 mm/min; ISO 527 |
| 79.0 MPa | 11500 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 5.2 % | 5.2 % | Type I, 50 mm/min; ASTM D638 |
| 7.6 % | 7.6 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 4.7 % | 4.7 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.78 GPa | 403 ksi | 5 mm/min; ASTM D638 |
| 3.11 GPa | 451 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 123 MPa | 17800 psi | 2 mm/min; ISO 178 |
| 125 MPa | 18100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.94 GPa | 426 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.97 GPa | 431 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.340 J/cm | 0.637 ft-lb/in | ASTM D256 |
| 0.270 J/cm @Temperature -30.0 °C |
0.506 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| 3.00 kJ/m² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 79.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 79.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C | 253 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 141 °C | 286 °F | Rate B/50; ISO 306 |
| 141 °C | 286 °F | Rate B/50; ASTM D1525 | |
| 142 °C | 288 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXD1414T PC Copolymer (Asia Pacific)
- PTS Tristar® PC-10FR-(VIK) 16 MFI Flame Retardant, UV Stabilized Polycarbonate With Impact Modifier and Release
- Iran Petrochemical (PCC) Tabriz 6630/1 High Impact Polystyrene (discontinued **)
- Lord Adhesives Thermosetâ„¢ UR-329 Two Component Urethane Potting Compound
- Karina 833D10/184-AY-IS-AS White PVC Compound
- Samyang Triloy® 120H PC/ABS alloy
- Arkema Group Rilsan® BESN P40 W5 TL Nylon 11, Flexible Tubing Grade (Conditioned)
- Austin Novel Materials Texalan® 490A Polyester-based TPU
- Overview of materials for Polyether Ester Elastomer
- Haynes Hastelloy® C-22® alloy, transverse, SMAW weldment, 19.1 mm thick plate