- Polycarbonate/ABS Alloy, Glass Fiber Filled
- SABIC Innovative Plastics LNP THERMOCOMP NF002 PC+ABS
SABIC Innovative Plastics LNP THERMOCOMP NF002 PC+ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP NF002 PC+ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* NF002 is a compound based on PC+ABS resin containing 10% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.130 % | 0.130 % | 50% RH, 24 hrs; ASTM D570 |
| 0.210 % | 0.210 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Time 86400 sec |
0.0030 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm @Time 86400 sec |
0.0050 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 78.0 MPa | 11300 psi | Type I, 5 mm/min; ASTM D638 |
| 78.0 MPa | 11300 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | 5 mm/min; ISO 527 |
| 81.0 MPa | 11700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 3.1 % | 3.1 % | Type I, 5 mm/min; ASTM D638 |
| 3.1 % | 3.1 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.9 % | 2.9 % | Type I, 5 mm/min; ASTM D638 |
| 2.9 % | 2.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.41 GPa | 640 ksi | 1 mm/min; ISO 527 |
| 4.81 GPa | 698 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 106 MPa | 15400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.16 GPa | 603 ksi | 2 mm/min; ISO 178 |
| 4.20 GPa | 609 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.18 J/cm | 2.21 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.94 J/cm | 9.25 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 19.0 J @Temperature 23.0 °C |
14.0 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 7.00 J | 5.16 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.2 µm/m-°C @Temperature -30.0 - 30.0 °C |
33.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 66.6 µm/m-°C @Temperature -30.0 - 30.0 °C |
37.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 241 PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics Lexan® FXD951A PC
- Karina Karintox 70 Polyolefin Compound
- SABIC Innovative Plastics LNP LUBRICOMP RAL23S PA 66
- Saint-Gobain Norprene® A-60-G Industrial Grade Tubing Formulation
- Solvay MIRATAINE® CBS-LR Surfactant
- Lubrizol STAT-RITE® E-1150 Ether-Type Static Dissipative Polymer
- Arkema Group Rilsan® Clear G350 Polyamide
- Premix Thermoplastics PRE-ELEC® PA 1409 Conductive Thermoplastic Compound
- Overview of materials for Polytrimethylene Terephthalate (PTT)
Copyright © lookpolymers.com All Rights Reserved