BASF Capron® 8224 HSL Nylon 6 (DAM) (discontinued **)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Capron® 8224 HSL Nylon 6 (DAM)
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Water Absorption | 1.6 % | 1.6 % | 24 hr.; ISO 62 |
| 9.5 % | 9.5 % | ISO 62 | |
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | 23°C/50% R.H.; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | 2 in/min; ASTM D638 |
| 79.0 MPa | 11500 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | >= 50 % | >= 50 % | 50 mm/min; Nominal; ISO 527 |
| >= 100 % | >= 100 % | 2 in/min; ASTM D638 | |
| Elongation at Yield | 10 % | 10 % | 50 mm/min; ISO 527 |
| 10 % | 10 % | 2 in/min; ASTM D638 | |
| Tensile Modulus | 3.00 GPa | 435 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 |
| 100 MPa | 14500 psi | ASTM D790 | |
| 8.00 MPa @Temperature 120 °C |
1160 psi @Temperature 248 °F |
ASTM D790 | |
| 179 MPa @Temperature -40.0 °C |
26000 psi @Temperature -40.0 °F |
ASTM D790 | |
| Flexural Modulus | 2.20 GPa | 319 ksi | ISO 178 |
| 2.45 GPa | 355 ksi | ASTM D790 | |
| 0.305 GPa @Temperature 120 °C |
44.2 ksi @Temperature 248 °F |
ASTM D790 | |
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in | ASTM D256 |
| 0.370 J/cm @Temperature -40.0 °C |
0.693 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |
| Charpy Impact Unnotched | 8.50 J/cm² | 40.5 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.410 J/cm² | 1.95 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 86.0 µm/m-°C @Temperature 20.0 °C |
47.8 µin/in-°F @Temperature 68.0 °F |
ASTM E831 |
| Melting Point | 220 °C | 428 °F | 10 K/min |
| 220 °C | 428 °F | ASTM D3418 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 167 °C | 333 °F | ASTM D648 |
| 178 °C | 352 °F | ISO 75 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| 60.0 °C | 140 °F | ISO 75 | |
| Oxygen Index | 23 % | 23 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Unfilled | |
| Attribute | Heat stabilized or stable to heat | |
| Color | Natural | |
| Commercial Status (March 2007) | Active America | |
| Form | Pellets | |
| Impact Modified | No | |
| Other Extrusion | Processable | |
| Primary Processing Technique | Wire and Cable | |
| Profile extrusion | Processable | |
| UL.UL-C | Yes |
Users viewing this material also viewed the following:
- Polimeros Mexicanos Rotolene® Natural Linear Medium Density Polyethylene
- DuPont Performance Polymers Delrin® FG400XRD NC010 Acetal (Unverified Data**)
- Grupo Repol Dinalon® B1S25 PA6 Unreinforced
- SABIC Innovative Plastics NORYL WCV072 PPE+PP (Europe-Africa-Middle East)
- Shandong Guangyin PA 610 Nylon Resin
- SABIC Innovative Plastics Xenoy® X4820 PBT+PC (Europe-Africa-Middle East)
- Shin-Etsu Silicones X-21-5595 Fluid
- Techmer ES HiFill® POM CO GF25 CC 25% Glass Filled
- SABIC Innovative Plastics Ultem ATX153R PEI+PCE (Europe-Africa-Middle East)
- DuPont Performance Polymers Zytel® HTN 51G35EF BK083 Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved