Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 56.9 MPa | 8250 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Rigid Extrusion 87707 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Rigid Extrusion 87717 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Rigid Extrusion 87727 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Rigid Extrusion 87727-0284 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples. Physical property testing was based on the Geon® 87727 Trans 0020.Information provided by PolyOne |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | ASTM D638 |
Polymer Resources PPX-GP2 Modified-PPO, General Purpose Modified-Polyphenylene Oxide, General Purpose, 250F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati.. |
|||
Tensile Strength, Yield | 56.9 MPa @Thickness 3.20 mm |
8250 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
LG Chemical Lupox® TE5000D PBT+PC Description: Injection Molding, PBT+PC, Good SurfaceApplication: E&E, Automotive (Lamp Housing)CAS No. 24968-12-5 and 103598-77-2Information provided by LG Chemical |
|||
Tensile Strength, Yield | 56.9 MPa @Thickness 3.20 mm |
8250 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
LG Chemical LUPOY EF5001RFT PC/ABS Description: Injection Molding, PC/ABS, Halogen Free Flame Retardant, EU Eco-Label compliantApplication: Display housingCAS: 103598-77-2, 9003-56-9 and 125997-21-9Information provided by LG Chemical.. |
|||
Tensile Strength, Yield | 56.9 MPa @Thickness 3.20 mm |
8250 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
LG Chemical LUPOY GP5006BH PC/ABS, Heat Resistance, Impact Strength Description: Injection Molding, PC/ABS, Heat Resistance, Impact Strength, High ToughnessApplication: Miscellaneous GoodsCAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provided by LG Chemical.. |
|||
Tensile Strength, Yield | 56.9 MPa @Thickness 3.20 mm |
8250 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
LG Chemical LUPOY NS5000 PC/ABS, High Impact Description: Injection Molding, PC/ABS, Heat Resistance, High Flow, High ImpactApplication: Automotive (Interior)CAS: 103598-77-2 and 9003-56-9Information provided by LG Chemical |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® AE-2130 PC/PET, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® CA-7009 PA/PPE, Antistatic Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® NH-1001T PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® BF-0930 MABS, Unreinforced Scratch Resistant Scratch resistantInformation provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® AE-2130 PC/PET, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® CA-7009 PA/PPE, Antistatic Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® HP-1000P PC/ABS, Unreinforced High flow material that can be used in the exterior material of mobile phone, wheel cap, rice cooker, electric iron etc. as well as refrigerator door handle and panelInformation provided by Samsung .. |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® QP-1010 PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® BF-0930 MABS, Unreinforced Scratch Resistant Scratch resistantInformation provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | ASTM D638 |
Samyang Triloy® 210 PC/ABS alloy Characteristics:Impact resistantHeat resistantGood flowApplications:Camera partsExterior panelCluster fasciaWheel coverStructural applicationI/P. core panelHelmet shellGlove box doorCowl vent grillA.. |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® HP-1000P PC/ABS, Unreinforced High flow material that can be used in the exterior material of mobile phone, wheel cap, rice cooker, electric iron etc. as well as refrigerator door handle and panelInformation provided by Samsung .. |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® HI-1001BN PC/ABS, Unreinforced PC/ABS that is used for the housing of mobile phone, wheel cap, rice cooker, electric iron etc., refrigerator door handle, panel etc.Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® LH-1070W PC, FR Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | ASTM D638 |
Cheng Yu Plastic SW15 POM/PTFE |
|||
Tensile Strength, Yield | 56.9 - 57.1 MPa | 8250 - 8280 psi | ASTM D638M |
DSM Somos® ProtoGen™ O-XT 18120 Epoxy Resin for Stereolithography, UV Postcure at HOC +3 DescriptionDSM Somos® ProtoGen O-XT 18120 is a liquid photopolymer that produces accurate parts ideal for general purpose applications. ProtoGen resins are the first SL resins to demonstrate diffe.. |
|||
Tensile Strength, Yield | 56.9 MPa @Thickness 3.20 mm |
8250 psi @Thickness 0.126 in |
Type 1, 5 mm/min; ASTM D-638 |
Bhansali Engineering Abstron IMG-1115 Glass Reinforced Grade Glass Reinforced ABS & SAN Resins for product specific requirement of very high rigidity and temperatureInformation provided by Bhansali |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | ASTM D638 |
Cheng Yu Plastic C1200 PC/ABS |
|||
Tensile Strength, Yield | 56.9 MPa @Thickness 3.20 mm |
8250 psi @Thickness 0.126 in |
Type 1, 5 mm/min; ASTM D-638 |
Bhansali Engineering Abstron IMG-1115 Glass Reinforced Grade Glass Reinforced ABS & SAN Resins for product specific requirement of very high rigidity and temperatureInformation provided by Bhansali |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® LH-1070W PC, FR Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 56.9 MPa | 8250 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® HN-1064IA PC, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 56.9 MPa @Thickness 3.20 mm |
8250 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
LG Chemical LUPOY SC1004ML PC, High Impact Description: Injection Molding, PC, General Purpose, High Impact, Good Coloring, Chemical ResistanceApplication: Mobile Phone HousingCAS: 103598-77-2 and 9046-16-6Information provided by LG Chemical.. |