Samyang Triloy® 210 PC/ABS alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Samyang |
| Trade Name | Triloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Triloy® 210 PC/ABS alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics:Impact resistantHeat resistantGood flowApplications:Camera partsExterior panelCluster fasciaWheel coverStructural applicationI/P. core panelHelmet shellGlove box doorCowl vent grillAll information provided by Samyang
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Water Absorption | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm |
0.0050 - 0.0070 in/in @Thickness 0.118 in |
ASTM D955 |
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 250 °C |
12 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Yield | 56.9 MPa | 8250 psi | ASTM D638 |
| Elongation at Break | 110 % | 110 % | ASTM D638 |
| Flexural Yield Strength | 81.4 MPa | 11800 psi | ASTM D790 |
| Flexural Modulus | 2.16 GPa | 313 ksi | ASTM D790 |
| Izod Impact, Unnotched | 7.35 J/cm @Thickness 3.17 mm |
13.8 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 73.0 µm/m-°C | 40.6 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.00e+16 ohm-cm | 5.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | ASTM D149 |
| Dissipation Factor | 0.0090 @Frequency 1.00e+6 Hz |
0.0090 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 123 sec | 123 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |
| Middle Barrel Temperature | 220 - 240 °C | 428 - 464 °F | |
| Front Barrel Temperature | 210 - 230 °C | 410 - 446 °F | |
| Nozzle Temperature | 240 - 250 °C | 464 - 482 °F | |
| Melt Temperature | 240 - 250 °C | 464 - 482 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Screw Speed | 30 - 80 rpm | 30 - 80 rpm |
Users viewing this material also viewed the following:
- Potters Industries Conduct-O-Fil® AG-SL150-16-TRD Silver-coated Hollow Ceramic Spheres
- Polymer Resources PC/ABS-FRG5 Flame Retardant PC/ABS Alloy, 5% Glass Reinforced
- SABIC Innovative Plastics LNP LUBRICOMP DL001 PC (Asia Pacific)
- Kraton® D1102 + LDPE blend (50/50)
- Multibase Multi-Flex® A 5003 TPE Thermoplastic Elastomer
- Zircar Refractory Composites RS-DM Refractory Sheet
- A. Schulman POLYAXIS® LPA815 LPA 815EVA
- Dow Saran® 8 Clear Plastic Barrier Film
- Ensinger HYDEX® 4101L Polybutylene Terephthalate (PBT)
Copyright © lookpolymers.com All Rights Reserved