Samsung Cheil Industries Infino® LH-1070W PC, FR

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Infino® LH-1070W PC, FR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.42 g/cc
1.42 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 65 g/10 min

@Load 10.0 kg,
Temperature 250 °C
 65 g/10 min

@Load 22.0 lb,
Temperature 482 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
ASTM D785
Tensile Strength at Break 46.1 MPa
6690 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 56.9 MPa
8250 psi
50 mm/min; ASTM D638
Elongation at Break 43 %
43 %
50 mm/min; ASTM D638
Tensile Modulus 2.16 GPa
313 ksi
50 mm/min; ASTM D638
Flexural Strength 83.4 MPa
12100 psi
2.8 mm/min; ASTM D790
Flexural Modulus 2.26 GPa
327 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched 1.47 J/cm

@Thickness 3.17 mm
 2.76 ft-lb/in

@Thickness 0.125 in
 ASTM D256
1.57 J/cm

@Thickness 6.35 mm
 2.94 ft-lb/in

@Thickness 0.250 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 131 °C

@Thickness 6.40 mm
 268 °F

@Thickness 0.252 in
 ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 122 °C

@Thickness 6.40 mm
 252 °F

@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 136 °C
277 °F
B/50; ISO R306
140 °C
284 °F
B/120; ISO R306
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in