LG Chemical Lupox® TE5000D PBT+PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | LG Chemical |
| Trade Name | Lupox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical Lupox® TE5000D PBT+PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PBT+PC, Good SurfaceApplication: E&E, Automotive (Lamp Housing)CAS No. 24968-12-5 and 103598-77-2Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm @Thickness 3.20 mm |
0.013 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 56.9 MPa @Thickness 3.20 mm |
8250 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 50 % @Thickness 3.20 mm |
>= 50 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 98.1 MPa @Thickness 6.40 mm |
14200 psi @Thickness 0.252 in |
5mm/min; ASTM D790 |
| Flexural Modulus | 2.26 GPa @Thickness 6.40 mm |
327 ksi @Thickness 0.252 in |
5mm/min; ASTM D790 |
| Izod Impact, Notched | 0.392 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.735 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | @ Break; ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 250 - 260 °C | 482 - 500 °F | Injection Molding |
| Middle Barrel Temperature | 250 - 260 °C | 482 - 500 °F | Injection Molding |
| Front Barrel Temperature | 255 - 265 °C | 491 - 509 °F | Injection Molding |
| Nozzle Temperature | 260 - 270 °C | 500 - 518 °F | Injection Molding |
| Melt Temperature | 260 - 270 °C | 500 - 518 °F | Injection Molding |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- PolyOne Syncure™ S1010B Polyethylene, Crosslinked (XLPE)
- Hong Kun Group 2-Methylindene Pharmaceutical Intermediate
- Multibase Multi-Flex® A 5904 LC TPE Thermoplastic Elastomer
- Techmer ES HiFill® PA6 GF20 RM BK 20% Glass Filled
- Styron CALIBREâ„¢ 303-06 Polycarbonate
- Trimay® Wear Plate TWP56 Chromium-based Flux Cored Weld Wire & Electrode
- Eastman Aspira EN177 Copolyester Resin for Extrusion Blow Molding
- Bohler-Uddeholm ORVAR® 2M / AISI H13 Hot Work Tool Steel
- Adamas Hardor® 991 PE-UHMW
- Ascend Performance Materials Vydyne® 66B, 66J Nylon 66, Conditioned (2.5% Moisture)
Copyright © lookpolymers.com All Rights Reserved