EMS-Grivory Grivory® HT3Z black 9564 PA*

Category	Polymer , Thermoplastic , Nylon
Manufacturer	EMS-Grivory (EMS-CHEMIE)
Trade Name	Grivory®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	EMS-Grivory Grivory® HT3Z black 9564 PA*.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product description: Grivory HT3Z is an unreinforced and impact resistant, engineering thermoplastic based on semi crystalline partially aromatic copolyamide. This Grivory HT product is partially based on renewable raw materials. ISO polymer designation: PA 10T/X ASTM designation: PPA, polyphthalamide Grivory HT3Z exhibits low moisture absorption, high stiffness and high heat distortion temperature.Information provided by EMS Grivory

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	ISO 1183
Water Absorption	2.6 %	2.6 %	ISO 62
Moisture Absorption	1.50 %	1.50 %	ISO 62
Linear Mold Shrinkage, Flow	0.020 cm/cm	0.020 in/in	ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.018 cm/cm	0.018 in/in	ISO 294-4, 2577

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	140 MPa	20300 psi	dry; ISO 2039-1
	140 MPa	20300 psi	conditioned; ISO 2039-1
Tensile Strength at Break	60.0 MPa	8700 psi	dry; ISO 527-1/-2
	60.0 MPa	8700 psi	conditioned; ISO 527-1/-2
Tensile Strength, Yield	80.0 MPa	11600 psi	conditioned; ISO 527-1/-2
	80.0 MPa	11600 psi	dry; ISO 527-1/-2
Elongation at Break	11 %	11 %	dry; ISO 527-1/-2
	11 %	11 %	conditioned; ISO 527-1/-2
Elongation at Yield	6.0 %	6.0 %	conditioned; ISO 527-1/-2
	6.0 %	6.0 %	dry; ISO 527-1/-2
Tensile Modulus	2.60 GPa	377 ksi	conditioned; ISO 527-1/-2
	2.60 GPa	377 ksi	dry; ISO 527-1/-2
Charpy Impact Unnotched	NB	NB	dry; ISO 179/1eU
	NB	NB	conditioned; ISO 179/1eU
	5.00 J/cm² @Temperature 30.0 °C	23.8 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU
	8.00 J/cm² @Temperature 30.0 °C	38.1 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
Charpy Impact, Notched	1.20 J/cm²	5.71 ft-lb/in²	dry; ISO 179/1eA
	1.20 J/cm²	5.71 ft-lb/in²	conditioned; ISO 179/1eA
	1.20 J/cm² @Temperature 30.0 °C	5.71 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
	1.20 J/cm² @Temperature 30.0 °C	5.71 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	80.0 µm/m-°C	44.4 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	80.0 µm/m-°C	44.4 µin/in-°F	ISO 11359-1/-2
Melting Point	295 °C	563 °F	10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air	140 °C	284 °F	long term; EMS
	240 °C	464 °F	short term; EMS
Deflection Temperature at 0.46 MPa (66 psi)	160 °C	320 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	115 °C	239 °F	ISO 75-1/-2
Flammability, UL94	HB	HB	IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+12 ohm-cm	1.00e+12 ohm-cm	dry; IEC 60093
	1.00e+12 ohm-cm	1.00e+12 ohm-cm	conditioned; IEC 60093
Surface Resistance	1.00e+11 ohm	1.00e+11 ohm	IEC 60093
Dielectric Strength	33.0 kV/mm	838 kV/in	dry; IEC 60243-1
	33.0 kV/mm	838 kV/in	conditioned; IEC 60243-1
Comparative Tracking Index	600 V	600 V	conditioned; IEC 60112

Descriptive Properties	Value	Comments
Automotive	Air intake sytems
	Automotive electr. and electronics, lighting
	Compressed air systems
	Fuel systems
	Hydraulic systems
	Interior
Electricals & Electronics	Connectors
	Electrical appliances
	Electrical equipment
	Energy distribution
	Lighting
	Mobile phones and other portable devices
Form	Granules
Industry & Consumer goods	Hydraulics & Pneumatics
	Mechanical Engineering
	Power transmission
	Tools & Accessories
Processing	Injection Molding
Product Attributes	Bio based Polyamide
	Co Polyamide
	Hydrolysis resistant
	Improved alcohol resistance
	Improved flowability and demoulding
	Partially aromatic Polyamide
	Transparent Polyamide
Special Characteristics	Flame retardant