LATI Laticonther 80 GR/50 PPS, 50% Graphite Reinforced
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | LATI |
| Trade Name | Laticonther |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Laticonther 80 GR/50 PPS, 50% Graphite Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High thermal conductivity product based on Polyphenylene Sulfide (PPS). Graphite. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.71 g/cc | 0.0618 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | |
| Elongation at Break | 0.60 % @Temperature 23.0 °C |
0.60 % @Temperature 73.4 °F |
|
| Tensile Modulus | 14.7 GPa | 2130 ksi | |
| Charpy Impact Unnotched | 0.500 J/cm² | 2.38 ft-lb/in² | |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 10.0 W/m-K | 69.4 BTU-in/hr-ft²-°F | Longitudinal |
| Maximum Service Temperature, Air | 220 °C | 428 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 275 °C | 527 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | |
| Vicat Softening Point | 245 °C @Load 5.00 kg |
473 °F @Load 11.0 lb |
|
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
|
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
||
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
||
| Glow Wire Test | 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
GWFI/GWT |
| 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
GWFI/GWT |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2000 ohm-cm | 2000 ohm-cm | |
| Surface Resistance | 600 ohm | 600 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 - 320 °C | 554 - 608 °F | |
| Mold Temperature | 130 - 140 °C | 266 - 284 °F | |
| Drying Temperature | 130 - 150 °C @Time 10800 sec |
266 - 302 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |