- SABIC Innovative Plastics LNP THERMOCOMP KF004AL Acetal Homopolymer
SABIC Innovative Plastics LNP THERMOCOMP KF004AL Acetal Homopolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Glass Fiber Reinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP KF004AL Acetal Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* KF004AL is a compound based on Acetal Homopolymer resin containing 20% Glass Fiber. Added features of this material include: Low Extractible.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm <br>@Time 86400 sec |
0.0040 in/in <br>@Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | 3.7 % | 3.7 % | ASTM D638 |
| Tensile Modulus | 8.61 GPa | 1250 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 4.21 J/cm | 7.89 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C <br>@Thickness 3.20 mm |
300 °F <br>@Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P2866T TPE, PP Overmold or Standalone use
- Nilit FRIANYL B63 L-HS-GV30 Nylon 6 for injection molding, 30% glass fiber reinforced
- MV Labs TM870 Tm2(C2O4)3·6H2O Thulium oxalate hydrate
- Kazanorgsintez 158-281 Low Density Polyethylene Composition with Improved Processibility
- Solvay Specialty Polymers Catalyst PS/2 UV Polyolefin
- Weartech International WT-50 Nickel Hardfacing & Wear Resistant Alloy
- Wellman Wellamid® GF13-66 22LH-NBK1 13% Glass Fiber Reinforced, General Purpose Nylon 66
- Ashley Polymers Ashlene® RH190-PF Acetal, PTFE Filled
- Resinlab® EP965LVLX Clear Unfilled Electronic Grade Epoxy Encapsulant
- Bhansali Engineering Abstron IM17SHG PMMA- ABS Alloy
Copyright © lookpolymers.com All Rights Reserved