Entec Hylex® P1017FR Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant |
| Manufacturer | Entec Engineered Resins |
| Trade Name | Hylex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Entec Hylex® P1017FR Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 17 g/10 min @Load 1.20 kg, Temperature 300 °C |
17 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | 110 % | 110 % | ASTM D638 |
| Flexural Strength | 96.5 MPa | 14000 psi | ASTM D790 |
| Flexural Modulus | 2.48 GPa | 360 ksi | ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm | 10.0 ft-lb/in | 73°F, 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 285 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 265 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | 0.0620 in, NA |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 243 - 266 °C | 470 - 510 °F | |
| Middle Barrel Temperature | 254 - 271 °C | 490 - 520 °F | |
| Front Barrel Temperature | 271 - 282 °C | 520 - 540 °F | |
| Nozzle Temperature | 266 - 277 °C | 510 - 530 °F | |
| Melt Temperature | 271 - 288 °C | 520 - 550 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 12 hour | 3 - 12 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Injection Pressure | 6.21 - 12.4 MPa | 900 - 1800 psi | |
| Back Pressure | 0.483 - 1.03 MPa | 70.0 - 150 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure | 600 to 1100 psi |
Users viewing this material also viewed the following:
- Orion Engineered Carbons CK3 Carbon Black
- SABIC Innovative Plastics Lexan® EXL1192T PC Copolymer (Europe-Africa-Middle East)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR N330 Filler
- LG Chemical LUPOS GP-2205NB General Purpose SAN, 20% Glass Fiber Reinforced, Dimensional Stability, Anti-Bacteria
- Kostat BK-STAT R048BK PS Sheet
- Teknor Apex Monprene® MP-1870-CR Thermoplastic Elastomer
- Chase Plastics CP Pryme® NN130GMD2HS (DAM) Nylon 66, 30% Glass Fiber Reinforced, 2% MoS2 Lubricated, Heat Stabilized
- Thermoseal KLINGERSIL® C-4509 Metal Reinforced Gasketing
- Radici Radilon® S LHS (dry) Nylon 6
Copyright © lookpolymers.com All Rights Reserved