SABIC Innovative Plastics Cycolac® INP581 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® INP581 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow, low molecular weight SAN.
Can be used as compounding additives for polymer blends.
Can be blended with high rubber graft modifier resins to produce customized ABS properties.
Suitable for direct weather exposure.
Provides excellent flow for demanding injection molding applications.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D 792 |
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Melt Flow | 37.7 g/10 min @Load 3.80 kg, Temperature 230 °C |
37.7 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D 1238 |
| 98 g/10 min @Load 10.0 kg, Temperature 220 °C |
98 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D 785 |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 1.9 % | 1.9 % | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Yield | 1.5 % | 1.5 % | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 4.08 GPa | 592 ksi | 5 mm/min; ASTM D 638 |
| Flexural Yield Strength | 36.0 MPa | 5220 psi | 2 mm/min; ISO 178 |
| 66.0 MPa | 9570 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 3.44 GPa | 499 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 3.52 GPa | 511 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.120 J/cm @Temperature -30.0 °C |
0.225 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 0.230 J/cm @Temperature 23.0 °C |
0.431 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 1.00 kJ/m² @Temperature 23.0 °C |
0.476 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| 1.00 kJ/m² @Temperature -30.0 °C |
0.476 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.100 J/cm² @Temperature 23.0 °C |
0.476 ft-lb/in² @Temperature 73.4 °F |
ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 102 °C | 216 °F | Rate B/50; ISO 306 |
| 104 °C | 219 °F | Rate B/120; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Yellow Index | 1.0 % | 1.0 % | ASTM D 1925 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 GF 35 Polyamide 66, 35% Glass Fiber
- Plenco 51240 PET, Pellet, Injection Molded, Green (discontinued **)
- Rogers Corporation Bisco® MF1 8055 - 55 Silicone, High Performance Foam, Indentation Force Material
- Shandong Dongyue Shenzhou New Material Co 3-methoxy-2,2,3,3-tetrafluoropropionatemethylester (MTPME)
- Williams Advanced Alloys WS290 Solder
- Eurotec® Tecoform® PO20 NL RW POM, surface modified, natural
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 20 PHR Fumed Silica - Wacker HK N20
- Haynes Hastelloy® C-22® alloy, GTAW, as welded, unnotched
Copyright © lookpolymers.com All Rights Reserved