SABIC Innovative Plastics Lexan® OQ3732 PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® OQ3732 PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Viscosity, UV-stabilized PC for ophthalmic lenses.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.35 % | 0.35 % | ISO 62 |
| Melt Index of Compound | 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 120 % | 120 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.35 GPa | 341 ksi | 1 mm/min; ISO 527 |
| 2.37 GPa | 344 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| 2.37 GPa | 344 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched (ISO) | 70.0 kJ/m² | 33.3 ft-lb/in² | 80*10*3; ISO 180/1A |
| 12.0 kJ/m² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 7.30 J/cm² | 34.7 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 143 °C | 289 °F | Rate B/50; ISO 306 |
| 145 °C | 293 °F | Rate B/120; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 0.40 % @Thickness 2.54 mm |
0.40 % @Thickness 0.100 in |
ASTM D1003 |
| Transmission, Visible | 87 % | 87 % | 2.54 mm; ASTM D1003 |
Users viewing this material also viewed the following:
- ND Industries SuperGlue Ethyl 322
- PolyMirae Moplen EP500N Injection Molding Grade Polypropylene
- Lord Adhesives 513 Fast Cure, Non-Sagging Acrylic Adhesive
- Solvay Chemicals Soda Solvay® Light Soda Ash (European Grade)
- Polyplastics Duranex® 711SA Polybutylene Terephthalate (PBT), Low density, Low wear, GF filled
- Carlson 317L 4N Austenitic Stainless Steel
- Arlon 940-07Rxx-P1 0.040" (1.02 mm) Self-Fusing Silicone Tape
- BASF Pluracol® 9346 Rigid Polyol
- Arkema Group Rilsan® BESN TL Nylon 11, Rigid Tubing Grade (Dry)
- Henkel Hysol EA 9394/C-2 Paste Adhesive System
Copyright © lookpolymers.com All Rights Reserved