- Chase Plastics CP Pryme® NN213GL (COND, 50% RH) Nylon 66, 13% Glass Fiber Reinforced, Internally Lubricated
Chase Plastics CP Pryme® NN213GL (COND, 50% RH) Nylon 66, 13% Glass Fiber Reinforced, Internally Lubricated
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled |
| Manufacturer | Chase Plastics |
| Trade Name | CP Pryme® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chase Plastics CP Pryme® NN213GL (COND, 50% RH) Nylon 66, 13% Glass Fiber Reinforced, Internally Lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chase Plastics.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.3 MPa | 10200 psi | ASTM D638 |
| Flexural Strength | 95.1 MPa | 13800 psi | ASTM D790 |
| Flexural Modulus | 2.48 GPa | 360 ksi | ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm | 2.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ASTM D648 |
Users viewing this material also viewed the following:
- SABIC PP 623B Polypropylene Random Co-polymer for Cast Film
- PolyOne Geon™ Vinyl Flexible R235AE White 1875 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Resin Technology Group TIGA 905 One-Part Silver Conductive Epoxy System
- Huntsman IROGRAN® A 70 H 4673 M Polyester-Based TPU-Injection Molding Grade
- Grupo Repol Dinalon® B1S25 M404 PA6 40% Mineral Charge
- Mearthane Durethaneâ„¢ S DS-385A Solid Polyurethane Elastomer
- Solvay Specialty Polymers Polymist® XPP 535 Polytetrafluoroethylene (PTFE)
- A. Schulman PAPERMATCH® T-4776/50 Specialty Masterbatch
- 3M 7897 Computer-Imprintable Polyester Label Material
Copyright © lookpolymers.com All Rights Reserved