- Wellman Wellamid® GS1861-N1(PTFE) Nylon 66, 35% Glass Sphere Reinforced, Enhanced Lubrication
Wellman Wellamid® GS1861-N1(PTFE) Nylon 66, 35% Glass Sphere Reinforced, Enhanced Lubrication
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Bead Filled |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | Wellamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman Wellamid® GS1861-N1(PTFE) Nylon 66, 35% Glass Sphere Reinforced, Enhanced Lubrication.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
All information provided by Wellman Engineered Resins.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183-87 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.014 cm/cm | 0.010 - 0.014 in/in | DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.013 cm/cm | 0.0090 - 0.013 in/in | DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527-93 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-93 |
| Flexural Strength | 115 MPa | 16700 psi | ISO 178-93 |
| Flexural Modulus | 4.10 GPa | 595 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75-93 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P1855 TPE, PP Overmold or Standalone use
- Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 285 Kevlar® Reinforced
- Radici Radilon® AHS (dry) Nylon 66
- MRC Polymers MAXNITE™ 500 GF15 PET, 15% Glass Fiber Filled (discontinued **)
- H.C. Starck Amperit® 538.074 Agglomerated, Sintered Tungsten Carbide-Tungsten Boride-Cobalt (WC-WB-Co ) 60-30-10
- DuPont Nucrel® 0902HC Ethylene-Methacrylic Acid Copolymer Resin for Blown and Cast Film
- Covestro Makroblend® S 7916/2 Polycarbonate + PBT, Impact Grade
- Entec Hyrene® PSCRY 8 General Purpose Polystyrene
- ExxonMobil Paxon™ AF50-003 Blow Molding Resin
Copyright © lookpolymers.com All Rights Reserved